Corrosion protection of AA6061 T6 10% Al2O3 composite by molybdate conversion coatings (Articolo in rivista)

Type
Label
  • Corrosion protection of AA6061 T6 10% Al2O3 composite by molybdate conversion coatings (Articolo in rivista) (literal)
Anno
  • 2005-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1007/s10800-004-8329-3 (literal)
Alternative label
  • A.S. Hamdy; A.M. Beccaria; P. Traverso (2005)
    Corrosion protection of AA6061 T6 10% Al2O3 composite by molybdate conversion coatings
    in Journal of Applied Electrochemistry; Springer, London (Regno Unito)
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • A.S. Hamdy; A.M. Beccaria; P. Traverso (literal)
Pagina inizio
  • 467 (literal)
Pagina fine
  • 472 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 35 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 5 (literal)
Note
  • Scopu (literal)
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • (1) Central Metallurgical R & D Institute, CMRDI, P.O. Box: 87, , Helwan, Cairo, Egypt; (2) Istituto per la Corrosione Marina dei Metalli - CNR, Via De Marini 6, 16149, Genova, Italy (3) Istituto per la Corrosione Marina dei Metalli - CNR, Via De Marini 6, 16149, Genova, Italy (2-3): queste affiliazioni sono quelle precedenti alla nascita dell' Istituto Nazionale I.S.MAR. (literal)
Titolo
  • Corrosion protection of AA6061 T6 10% Al2O3 composite by molybdate conversion coatings (literal)
Abstract
  • The corrosion protection performance of aluminum composite materials was investigated in 3.5% NaCl solution for time ranging between 1-60 days. Series of specimens were treated in molybdate solutions under different conditions. Free immersion and electrochemical activation techniques were used to apply the molybdate layer. The specimens which were directly treated or pickled before molybdate treatment showed severe pitting corrosion. Conversely, the specimens which were subjected to an oxide thickening step before the molybdate treatment showed outstanding corrosion protection. XPS revealed a higher amount of molybdate as MoO4 2- for the specimens prepared by electrochemical activation technique than for the free immersion technique. (literal)
Editore
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Prodotto
Autore CNR di
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Editore di
Insieme di parole chiave di
data.CNR.it