High-Temperature Resistant Composites in the AlN?SiC?MoSi2 System?, J. Am. Ceram. Soc. (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• High-Temperature Resistant Composites in the AlN?SiC?MoSi2 System?, J. Am. Ceram. Soc. (Articolo in rivista) (literal)

Anno

• 2003-01-01T00:00:00+01:00 (literal)

Alternative label

• D. Sciti, S. Guicciardi, C. Melandri, A. Bellosi (2003)
  High-Temperature Resistant Composites in the AlN?SiC?MoSi2 System?, J. Am. Ceram. Soc.
  in Journal of the American Ceramic Society
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• D. Sciti, S. Guicciardi, C. Melandri, A. Bellosi (literal)

Pagina inizio

• 1720 (literal)

Pagina fine

• 1726 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 86 (literal)

Rivista

• Journal of the American Ceramic Society (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#descrizioneSinteticaDelProdotto

• L'articolo descrive la produzione e la caratterizzazione termo-meccanica di un composito ceramico elettroconduttore. Oltre alla dimostrata capacità nell'ottenimento di un composito con rilevanti proprietà elettriche e strutturali, queste ultime anche ad alta temperatura, l'articolo si segnala per l'analisi effettuata sui dati sperimentali misurati mediante i modelli teorici relativi alle proprietà dei compositi. Nonostante la complessa microstruttura propria dei compositi ceramici, la possibilità di comparare le risultanze sperimentali con stime effettuate a priori permette la conferma della rispondenza delle proprietà del composito in esame con quelle attese. L'accertamento e la comprensione degli eventuali scostamenti forniscono quindi informazioni che possono essere utilizzate o per il feed-back del processo di ottimizzazione del composito in questione o per ulteriori indagini che esaminino i fenomeni inattesi che hanno generato il divario tra teoria ed esperimenti. (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Istituto di Scienza e Tecnologia per i Materiali Ceramici (ISTEC) del CNR (literal)

Titolo

• High-Temperature Resistant Composites in the AlN?SiC?MoSi2 System?, J. Am. Ceram. Soc. (literal)

Abstract

• Two fully dense composites containing AlN, SiC and MoSi2 in different amounts were produced by hot pressing. The main phase is AlN, SiC content is 15 and 20 vol % and MoSi2 content is 20 and 30 vol % in the two composites, respectively. Young modulus, hardness, electrical conductivity and thermal expansion coefficient were measured at room temperature. Strength and toughness were evaluated up to 1300°C in air. From statistical analysis, the temperature has little or no effect on high-temperature fracture behavior of the composites. These electroconductive materials are suitable for thermo-mechanical applications at high temperature, being the strength at 1300°C about 600 MPa. (literal)

Prodotto di

• Institute of science and technology for ceramics (ISTEC) (Istituto)

Autore CNR

• ALIDA BELLOSI (Persona)
• DILETTA SCITI (Unità di personale interno)
• CESARE MELANDRI (Unità di personale interno)
• STEFANO GUICCIARDI O GUIZZARDI (Persona)

Insieme di parole chiave

• Parole chiave di "High-Temperature Resistant Composites in the AlN?SiC?MoSi2 System?, J. Am. Ceram. Soc." (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute of science and technology for ceramics (ISTEC) (Istituto)

Autore CNR di

• DILETTA SCITI (Unità di personale interno)
• ALIDA BELLOSI (Persona)
• STEFANO GUICCIARDI O GUIZZARDI (Persona)
• CESARE MELANDRI (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of the American Ceramic Society (Rivista)

Insieme di parole chiave di

• Parole chiave di "High-Temperature Resistant Composites in the AlN?SiC?MoSi2 System?, J. Am. Ceram. Soc." (Insieme di parole chiave)