Electron microscopy evidence of aggregation under three different size scales for soot nanoparticles in flame (Articolo in rivista)

Type
Label
  • Electron microscopy evidence of aggregation under three different size scales for soot nanoparticles in flame (Articolo in rivista) (literal)
Anno
  • 2001-01-01T00:00:00+01:00 (literal)
Alternative label
  • di Stasio S. (2001)
    Electron microscopy evidence of aggregation under three different size scales for soot nanoparticles in flame
    in Carbon
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • di Stasio S. (literal)
Pagina inizio
  • 109 (literal)
Pagina fine
  • 118 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 39 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#descrizioneSinteticaDelProdotto
  • Evidenza sperimentale riportata per la prima volta in letteratura circa il verificarsi, in fiamme a diffusione, di processi di aggregazione di nanoparticelle di soot su tre diverse scale di lunghezza. In particolare, sono state osservate tre classi di nanoparticelle di nerofumo. La prima classe costituita dalle note particelle primarie (20-50 nm), che sono riportate in letteratura essere le sub-unità (sfere primarie o monomeri) costituenti gli aggregati di nerofumo. Le altre due classi di nanoparticelle osservate sono state chiamate \"sub-primarie\" (sub-primary, dimensione 6-9 nm) e \"particelle elementari\" (elementary particles, dimensione minore di 5 nm). Le particelle subprimarie sono apparse essere di tipo grafitico, di forma ellissoidale e aggregate l'una con l'altra per formare piccole catene al più composte da una decina di unità. Le particelle elementari sono state osservate essere costituite da gusci sferici di forma molto regolare (circa 4 nm) composti di carbonio amorfo e da nuclei interni di dimensioni circa 0.5-2 nm di tipo grafitico. (literal)
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • Istituto Motori, CNR, Napoli. (literal)
Titolo
  • Electron microscopy evidence of aggregation under three different size scales for soot nanoparticles in flame (literal)
Abstract
  • The microstructure of soot at larger (~1 s) residence times within a propane-air diffusion flame is here investigated by Transmission Electron Microscopy. Three classes of nanoparticles are observed. The first of them is recognised as the well-known class of primary particles (20-50 nm) that usually are reported to be the sub-units constituting the chain-like and fractal soot aggregates. The other two categories of carbon nanoparticles here evidenced are distinguished in sub-primary graphitical particles (6-9 nm) and elementary particles, (less than 5 nm). Sub-primaries appear to be graphite-like, ellipsoidal in shape and clustered together to form small chains of less than ten units. Elementary particles appear to be constituted by very regularly sized transparent shells (~ 4 nm) of amorphous carbon and by inner graphitic nuclei (~0.5-2 nm). Elementary particles are often observed to be closely packed together and to fill all the available space between graphitic layers and larger particles. Aggregation of sub-primary with primary particles is also observed to occur. Vesicle-like structures of external dimension about 15 nm with a shell about 5 nm thick, and short tubular structures of length 5-10 nm and diameter 0.5-1 nm are episodically individuated in TEM micrographs. Major result can be summarised in the evidence of a strongly polydispersed agglomeration mechanism occurring under three different scales of particle size. Implications of such a result, in terms of coagulation times for each of the observed nanoparticle typology are also discussed. (literal)
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Prodotto
Autore CNR di
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Insieme di parole chiave di
data.CNR.it