Nickel nanostructured materials from liquid phase photodeposition (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Nickel nanostructured materials from liquid phase photodeposition (Articolo in rivista) (literal)

Anno

• 2007-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1007/s11051-006-9089-2 (literal)

Alternative label

• Giuffrida S, Condorelli GG, Costanzo LL, Ventimiglia G, Lo Nigro R, Favazza M, Votrico E, Bongiorno C, Fragala IL (2007)
  Nickel nanostructured materials from liquid phase photodeposition
  in Journal of nanoparticle research
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Giuffrida S, Condorelli GG, Costanzo LL, Ventimiglia G, Lo Nigro R, Favazza M, Votrico E, Bongiorno C, Fragala IL (literal)

Pagina inizio

• 611 (literal)

Pagina fine

• 619 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 9 (literal)

Rivista

• Journal of nanoparticle research (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 9 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Univ Catania, Dipartimento Sci, I-95125 Catania, Italy; INSTM, UdR Catania, I-95125 Catania, Italy; CNR-IMM, I-95125 Catania, Italy (literal)

Titolo

• Nickel nanostructured materials from liquid phase photodeposition (literal)

Abstract

• Liquid Phase Photo-Deposition (LPPD) technique has been used to obtain both colloidal particles and thin films of metallic and chloride nickel from solutions of only precursor Ni(acac)(2) (acac=2,4-pentandionato). Metallic nickel was obtained from ethanol solutions by direct nickel(II) photoreduction at 254 nm and by acetone sensitised reaction at 300 nm. In this latter process the rate was higher than in the first one. NiCl2 was formed from CCl4 solution by a solvent-initiated reaction. TEM analysis, performed on colloidal particles of nickel, showed that their dimensions are in the range 2-4 nm. The films did not present carbon contamination and were characterized by AFM, XPS and GIXRD. Metallic films consisted of particles of 20-40 nm that are the result of the aggregation of smaller crystallites (4-5 nm). Larger agglomerations (around 200 nm) have been observed for NiCl2 films. (literal)

Prodotto di

• Institute for microelectronics and microsystems (IMM) (Istituto)
• Materiali multifunzionali, e innovativi per componenti integrati (MD.P05.003.002) (Modulo)

Autore CNR

• RAFFAELLA LO NIGRO (Unità di personale interno)
• CORRADO BONGIORNO (Unità di personale interno)

Insieme di parole chiave

• Keywords of "Nickel nanostructured materials from liquid phase photodeposition" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute for microelectronics and microsystems (IMM) (Istituto)
• Materiali multifunzionali, e innovativi per componenti integrati (MD.P05.003.002) (Modulo)

Autore CNR di

• RAFFAELLA LO NIGRO (Unità di personale interno)
• CORRADO BONGIORNO (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of nanoparticle research (Rivista)

Insieme di parole chiave di

• Keywords of "Nickel nanostructured materials from liquid phase photodeposition" (Insieme di parole chiave)