Preparation and characterization of powders and crystals of Vn-xTixO2n-1 Magneli oxides (Articolo in rivista)

Type
Label
  • Preparation and characterization of powders and crystals of Vn-xTixO2n-1 Magneli oxides (Articolo in rivista) (literal)
Anno
  • 2005-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1002/crat.200410488 (literal)
Alternative label
  • Calestani D.; Licci F.; Kopnin E.; Calestani G.; Gauzzi A.; Bolzoni F.; Besagni T.; Boffa V.; Marezio M. (2005)
    Preparation and characterization of powders and crystals of Vn-xTixO2n-1 Magneli oxides
    in Crystal research and technology (1981)
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Calestani D.; Licci F.; Kopnin E.; Calestani G.; Gauzzi A.; Bolzoni F.; Besagni T.; Boffa V.; Marezio M. (literal)
Pagina inizio
  • 1067 (literal)
Pagina fine
  • 1071 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 40 (literal)
Rivista
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • IMEM-CNR, Area delle Scienze 37/A, 43010 Parma, Italy Pirelli Labs, Viale Sarca 222, 20126 Milano, Italy Università di Parma, Dipartimento di Chimica, Area delle Scienze, Parma, Italy CRETA-CNRS, 25 Av. Des Martyrs, 38042 Grenoble, France (literal)
Titolo
  • Preparation and characterization of powders and crystals of Vn-xTixO2n-1 Magneli oxides (literal)
Abstract
  • Vn-xTixO2n-1 Magnéli phases have been synthesized under vacuum in powder form (n=4, 0<=x<=0.4) and crystals (n = 4 and 5, x = 0.5 and 1.4, respectively), grown by chemical vapour transport in closed ampoules. TeCl4 and NH4Cl were used as transporting agents. Needle-shaped crystals as long as 200-300 micrometers or 2-3 mm were obtained when in presence of NH4Cl or TeCl4, respectively. The powder and crystal structures were examined by X-ray diffraction and the transport and magnetic characteristics were measured.. The powders resulted to be single-phase and the relevant composition was assumed to be equal to the nominal one. The overall stoichiometry of compounds, n, was determined from single crystal X-ray diffraction data. The Ti content, x, was deduced from the elementary cell volume, by applying the Végard law. Crystals were mainly untwinned and of good quality. The elementary cell of both, powders and crystals, was triclinic (P-1) and did not change with doping. DC electrical resistivity of the crystals was measured in a four-points (van der Pauw) configuration. DC magnetic susceptibility of the powders was measured in a SQUID magnetometer. The Ti doping was found to progressively smooth and finally to suppress the magnetic transitions occurring in the V4O7. The metal-insulator transitions observed in V4O7 and V5O9, at around 235 and 125 K respectively, were not observed in the doped crystals, thus indicating some significant change of the electronic structure of the V oxides. (literal)
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Autore CNR di
Prodotto
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Insieme di parole chiave di
data.CNR.it