Fs-laser processing of polydimethylsiloxane (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Fs-laser processing of polydimethylsiloxane (Articolo in rivista) (literal)

Anno

• 2014-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1063/1.4887812 (literal)

Alternative label

• Atanasov, Petar A.; Nedyalkov, Nikolay N.; Valova, Eugenia I.; Georgieva, Zhenya S.; Armyanov, Stefan A.; Kolev, Konstantin N.; Amoruso, Salvatore; Wang, Xuan; Bruzzese, Ricardo; Sawczak, Miroslaw; Sliwinski, Gerard (2014)
  Fs-laser processing of polydimethylsiloxane
  in Journal of applied physics
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Atanasov, Petar A.; Nedyalkov, Nikolay N.; Valova, Eugenia I.; Georgieva, Zhenya S.; Armyanov, Stefan A.; Kolev, Konstantin N.; Amoruso, Salvatore; Wang, Xuan; Bruzzese, Ricardo; Sawczak, Miroslaw; Sliwinski, Gerard (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 116 (literal)

Rivista

• Journal of applied physics (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 4 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 2 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Bulgarian Academy of Sciences; Bulgarian Academy of Sciences; University of Naples Federico II; Polish Academy of Science (literal)

Titolo

• Fs-laser processing of polydimethylsiloxane (literal)

Abstract

• We present an experimental analysis on surface structuring of polydimethylsiloxane films with UV (263 nm) femtosecond laser pulses, in air. Laser processed areas are analyzed by optical microscopy, SEM, and mu-Raman spectroscopy. The laser-treated sample shows the formation of a randomly nanostructured surface morphology. mu-Raman spectra, carried out at both 514 and 785nm excitation wavelengths, prior and after laser treatment allow evidencing the changes in the sample structure. The influence of the laser fluence on the surface morphology is studied. Finally, successful electro-less metallization of the laser-processed sample is achieved, even after several months from the laser-treatment contrary to previous observation with nanosecond pulses. Our findings address the effectiveness of fs-laser treatment and chemical metallization of polydimethylsiloxane films with perspective technological interest in micro-fabrication devices for MEMS and nano-electromechanical systems. (C) 2014 AIP Publishing LLC. (literal)

Prodotto di

• Crescita e caratterizzazioni magnetiche, ottiche e di trasporto di film e multistrati epitassiali o nanostrutturati (MD.P04.025.002) (Modulo)

Autore CNR

• RICCARDO BRUZZESE (Persona)
• XUAN WANG (Unità di personale interno)
• SALVATORE AMORUSO (Unità di personale esterno)

Incoming links:

Autore CNR di

• XUAN WANG (Unità di personale interno)
• SALVATORE AMORUSO (Unità di personale esterno)
• RICCARDO BRUZZESE (Persona)

Prodotto

• Crescita e caratterizzazioni magnetiche, ottiche e di trasporto di film e multistrati epitassiali o nanostrutturati (MD.P04.025.002) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of applied physics (Rivista)