Nano-TiO2 Particles Produced in a Vapour-Fed Aerosol Flame Reactor (Abstract/Comunicazione in atti di convegno)

Type
Label
  • Nano-TiO2 Particles Produced in a Vapour-Fed Aerosol Flame Reactor (Abstract/Comunicazione in atti di convegno) (literal)
Anno
  • 2013-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.4405/36proci2013.VII3 (literal)
Alternative label
  • G. De Falco, M. Commodo, A. Santamaria, P. Minutolo, A. D'Anna (2013)
    Nano-TiO2 Particles Produced in a Vapour-Fed Aerosol Flame Reactor
    in XXXVI Meeting of the Italian Section of the Combustion Institute, Isola di Procida, Napoli, Italy, 13-15 June 2013
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • G. De Falco, M. Commodo, A. Santamaria, P. Minutolo, A. D'Anna (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#titoloVolume
  • Proceedings of XXXVI Meeting of the Italian Section of the Combustion Institute (literal)
Note
  • Comunicazione (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • * Dipartimento di Ingegneria Chimica, dei Materiali e della Produzione Industriale - Università degli Studi di Napoli Federico II, Napoli, Italy ** Istituto di Ricerche sulla Combustione - C.N.R., Napoli, Italy *** Instituto de Quimica - Universidad de Antioquia, Medellin, Colombia (literal)
Titolo
  • Nano-TiO2 Particles Produced in a Vapour-Fed Aerosol Flame Reactor (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#isbn
  • 9788888104157 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autoriVolume
  • A. Ciajolo, A. D'Anna, G. Nathan, F. Scala (literal)
Abstract
  • Nanoparticles of titanium dioxide were produced in a vapour-fed aerosol flame reactor by feeding ethanol solutions of titanium tetraisopropoxide (TTIP) in a premixed laminar flame of ethylene and air. The synthesized samples was characterized by Differential Mobility Analizer (DMA), Raman scattering, UV-Visible absorption and Photoluminescence (PL) spectroscopy. As-prepared nanoparticles appeared to be pure anatase crystallite of 1.7-3.1 nm in diameter, depending on TTIP concentration in the precursor solution. Optical band gap value of TiO2 particles was calculated to be 3.15 eV, and photoluminescence in the ultra-violet region, extending also to the visible spectral region, was observed. (literal)