Wool fibres functionalized with a silane-based coupling agent for reinforced polypropylene composites (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Wool fibres functionalized with a silane-based coupling agent for reinforced polypropylene composites (Articolo in rivista) (literal)

Anno

• 2014-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.compositesa.2014.02.005 (literal)

Alternative label

• L. Conzatti, F. Giunco, P. Stagnaro, A. Patrucco, C. Tonin, C. Marano, M. Rink, E. Marsano (2014)
  Wool fibres functionalized with a silane-based coupling agent for reinforced polypropylene composites
  in Composites. Part A, Applied science and manufacturing
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• L. Conzatti, F. Giunco, P. Stagnaro, A. Patrucco, C. Tonin, C. Marano, M. Rink, E. Marsano (literal)

Pagina inizio

• 51 (literal)

Pagina fine

• 59 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://www.sciencedirect.com/science/article/pii/S1359835X14000451 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 61 (literal)

Rivista

• Composites. Part A, Applied science and manufacturing (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 8 (literal)

Note

• ISI Web of Science (WOS) (literal)
• Scopu (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• CNR ISMAC Genova CNR ISMAC Biella Politecnico di Milano Università di Genova (literal)

Titolo

• Wool fibres functionalized with a silane-based coupling agent for reinforced polypropylene composites (literal)

Abstract

• Polypropylene (PP)-based composites containing 20 wt.% wool fibres were successfully prepared using a simple melt blending procedure. A blend of a commercial-grade PP and a maleinised PP was chosen as the matrix. To investigate the effects of modifying the fibre surface on the fibre/matrix adhesion, wool fibres were used as received, oxidised, or functionalised with a silane-based coupling agent, capable in principle of reacting with both the fibres and the polyolefinic matrix. The silanisation of the fibres and the consequent surface modifications were assessed using infrared spectroscopy and scanning electron microscopy. The resulting PP-based composites were thoroughly characterised in terms of their morphology, thermal stability and mechanical behaviour. (literal)

Prodotto di

• Progettazione e sviluppo di materiali polimerici multifasici micro e nanostrutturati (PM.P02.005.004) (Modulo)
• Materiali tessili, Tecnofibre e Processi industriali per la filiera tessile (SP.P01.031.001) (Modulo)
• Istituto per lo studio delle macromolecole (ISMAC) (Istituto)

Autore CNR

• ALESSIA PATRUCCO (Persona)
• CLAUDIO TONIN (Unità di personale interno)
• FRANCESCO GIUNCO (Unità di personale esterno)
• PAOLA STAGNARO (Persona)
• LUCIA CONZATTI (Unità di personale interno)

Incoming links:

Prodotto

• Istituto per lo studio delle macromolecole (ISMAC) (Istituto)
• Materiali tessili, Tecnofibre e Processi industriali per la filiera tessile (SP.P01.031.001) (Modulo)
• Progettazione e sviluppo di materiali polimerici multifasici micro e nanostrutturati (PM.P02.005.004) (Modulo)

Autore CNR di

• PAOLA STAGNARO (Persona)
• CLAUDIO TONIN (Unità di personale interno)
• LUCIA CONZATTI (Unità di personale interno)
• FRANCESCO GIUNCO (Unità di personale esterno)
• ALESSIA PATRUCCO (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Composites. Part A, Applied science and manufacturing (Rivista)