Improvements in the production of Yb:YAG transparent ceramic materials:Spray drying optimization (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Improvements in the production of Yb:YAG transparent ceramic materials:Spray drying optimization (Articolo in rivista) (literal)

Anno

• 2012-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.optmat.2011.06.003 (literal)

Alternative label

• Serantoni, Marina; Piancastelli, Andreana; Costa, Anna Luisa; Esposito, Laura (2012)
  Improvements in the production of Yb:YAG transparent ceramic materials:Spray drying optimization
  in Optical materials (Amst., Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Serantoni, Marina; Piancastelli, Andreana; Costa, Anna Luisa; Esposito, Laura (literal)

Pagina inizio

• 995 (literal)

Pagina fine

• 1001 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#altreInformazioni

• ID_PUMA: cnr.istec/2012-A0-027. Area di valutazione: 03 - Scienze chimiche. 6th Laser Ceramics Symposium (LCS) Location: Munster Univ Appl Sci, Munster, GERMANY Date: DEC 06-08, 2010. (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://dx.doi.org/10.1016/j.optmat.2011.06.003 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 34 (literal)

Rivista

• Optical materials (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 7 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 6 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• CNR-ISTEC, Faenza (literal)

Titolo

• Improvements in the production of Yb:YAG transparent ceramic materials:Spray drying optimization (literal)

Abstract

• Spray drying parameters have been optimized for the preparation of granulated stoichiometric mixture of oxides. These oxides are used in the production of Yb:YAG laser grade ceramic materials by reactive sintering. The selected compositions were Yb0.294Y2.706Al5O12 and Yb0.03Y2.97Al5O12, i.e. YAG doped with 9.8 and 1.0 at% of Yb with respect to the overall Y + Yb amount. The influence of solid content, drying medium flux, temperature and aspiration rate of the spray drying process on the transparency of the sintered materials has been evaluated. Sintering was conducted under high vacuum and clean atmosphere in the temperature range of 1650-1735°?C and with a soaking time of 16h. SEM analysis of the microstructure of granulated powders and sintered materials, as well as the transmittance measurement, were used as tools to guide the selection of the best spray drying parameters. (literal)

Prodotto di

• Materiali ceramici trasparenti per applicazioni ottiche ed elettromagnetiche (SP.P01.033.003) (Modulo)
• Institute of science and technology for ceramics (ISTEC) (Istituto)

Autore CNR

• ANNA LUISA COSTA (Persona)
• MARINA SERANTONI (Unità di personale esterno)
• LAURA ESPOSITO (Unità di personale interno)
• ANDREANA PIANCASTELLI (Unità di personale interno)

Insieme di parole chiave

• Keywords of "Improvements in the production of Yb:YAG transparent ceramic materials:Spray drying optimization" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Materiali ceramici trasparenti per applicazioni ottiche ed elettromagnetiche (SP.P01.033.003) (Modulo)

Autore CNR di

• LAURA ESPOSITO (Unità di personale interno)
• ANDREANA PIANCASTELLI (Unità di personale interno)
• MARINA SERANTONI (Unità di personale esterno)
• ANNA LUISA COSTA (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Optical materials (Rivista)

Insieme di parole chiave di

• Keywords of "Improvements in the production of Yb:YAG transparent ceramic materials:Spray drying optimization" (Insieme di parole chiave)