Preparation and dielectric properties of BaZr0.1Ti0.9O3 ceramics with different grain sizes (Articolo in rivista)

Type

Label

Preparation and dielectric properties of BaZr0.1Ti0.9O3 ceramics with different grain sizes (Articolo in rivista) (literal)

Anno

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

Alternative label

C. E. CIOMAGA; M. T. BUSCAGLIA; M. VIVIANI; V. BUSCAGLIA; L. MITOSERIU; A. STANCU; P. NANNI (2006)
Preparation and dielectric properties of BaZr0.1Ti0.9O3 ceramics with different grain sizes
in Phase transitions (Online); Taylor & Francis Ltd., Abingdon (Regno Unito)
(literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

C. E. CIOMAGA; M. T. BUSCAGLIA; M. VIVIANI; V. BUSCAGLIA; L. MITOSERIU; A. STANCU; P. NANNI (literal)

Pagina inizio

Pagina fine

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

http://puma.isti.cnr.it/linkres.php?resource=cnr.ieni/cnr.ieni.ge/2006-A0-025 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

Rivista

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#note

In: Phase Transitions, vol. 79 (6-7) pp. 389-397. Taylor & Francis Group, 2006. (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

Note

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

Solid State & Theoretical Physics Department, Al. I. Cuza Univ., Bv. Carol I no. 11, Iasi, 700506, RomaniA; Institute for Energetics & Interphases - CNR, Via de Marini no. 6, Genoa I-16149, Italy; Department of Chemistry & Proc. Eng., University of Genoa, P-le Kennedy 1, Genoa I-16129, Italy (literal)

Titolo

Preparation and dielectric properties of BaZr0.1Ti0.9O3 ceramics with different grain sizes (literal)

Abstract

BaZr0.1Ti0.9O3 ceramics with grain sizes of 0.75 and 2.60 µm have been prepared via solid-state reaction. Optimum parameters for calcination and sintering have been found in order to obtain pure perovskite phase, high density ceramics and homogeneous microstructures. The dielectric data show a diffuse phase transition with a mixed ferroelectric-relaxor character at a maximum at 87-92°C, with a small thermal hysteresis of 2-3°C. A tendency towards a more diffuse character of the ferro-para phase transition towards the full relaxor behaviour is observed as small in the ceramic grain size. Better dielectric properties in the coarse ceramics with higher permittivity up to 14,000 at the transition temperature by comparison with 5000 for the fine one, are observed as a consequence of higher tetragonal distortion and higher density. The differences in the dielectric spectra found for the two grain sizes were interpreted as a consequence of the higher degree of inhomogeneity in the fine ceramics and to different grain boundary properties induced by the different sintering temperatures. (literal)