Structural and morphological investigation of Ce0.6Zr0.4O2 oxides synthesized by sol-gel method: Influence of calcination and redox treatments (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Structural and morphological investigation of Ce0.6Zr0.4O2 oxides synthesized by sol-gel method: Influence of calcination and redox treatments (Articolo in rivista) (literal)

Anno

• 2003-01-01T00:00:00+01:00 (literal)

Alternative label

• Liotta L.F., Macaluso A., Pantaleo G., Longo A., Martorana A., Deganello, G., Marcì G. , Gialanella S. (2003)
  Structural and morphological investigation of Ce0.6Zr0.4O2 oxides synthesized by sol-gel method: Influence of calcination and redox treatments
  in Journal of sol-gel science and technology
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Liotta L.F., Macaluso A., Pantaleo G., Longo A., Martorana A., Deganello, G., Marcì G. , Gialanella S. (literal)

Pagina inizio

• 235 (literal)

Pagina fine

• 240 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 26 (literal)

Rivista

• Journal of sol-gel science and technology (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 1 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• ISMN-CNR, Sez. Palermo (ISMN-Palermo), via Ugo La Malfa, 153, 90146 Palermo, Italy Dipto. Chim. Inorg./Chim. A.S.C., Universitè di Palermo, Viale delle Scienze, 90128 Palermo, Italy Dipto. Ingegneria Chim. Proc./Mat., Università di Palermo, Viale delle Sci., Parco d'Orleans II, 90128 Palermo, Italy Dipto. di Ingegneria dei Mat., Università degli Studi Trento, 38050 Mesiano, Trento, Italy (literal)

Titolo

• Structural and morphological investigation of Ce0.6Zr0.4O2 oxides synthesized by sol-gel method: Influence of calcination and redox treatments (literal)

Abstract

• Ceria-zirconia mixed oxides of nominal composition Ce0.6Zr0.4O2 were prepared by sol-gel method. The structural and morphological modifications of these materials due to calcination and redox treatments up to 1000°C were studied by X-ray diffraction (XRD) and Rietveld refinements, specific surface area measurements (BET), oxygen storage capacity (OSC), TEM and SEM analyses. The materials maintain high OSC after several hours of treatments at 1000°C in oxidizing and reducing atmosphere, showing good resistance to the thermal ageing. An improvement of the OSC is manifested after repetitive redox cycles, even though textural characterization shows that reduction/oxidation processes induce sintering of the crystallites. (literal)

Prodotto di

• Istituto per lo studio dei materiali nanostrutturati (ISMN) (Istituto)

Autore CNR

• LEONARDA FRANCESCA LIOTTA (Unità di personale interno)
• ALESSANDRO LONGO (Unità di personale interno)
• GIUSEPPE PANTALEO (Persona)

Incoming links:

Prodotto

• Istituto per lo studio dei materiali nanostrutturati (ISMN) (Istituto)

Autore CNR di

• LEONARDA FRANCESCA LIOTTA (Unità di personale interno)
• ALESSANDRO LONGO (Unità di personale interno)
• GIUSEPPE PANTALEO (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of sol-gel science and technology (Rivista)