Cathodic deposition of ternary In+As+Sb alloys and formation of InAsxSb1-x (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Cathodic deposition of ternary In+As+Sb alloys and formation of InAsxSb1-x (Articolo in rivista) (literal)

Anno

• 1995-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/0022-0728(94)03604-2 (literal)

Alternative label

• Cattarin S.; Musiani M.M.; Casellato U.; Guerriero P.; Bertoncello R. (1995)
  Cathodic deposition of ternary In+As+Sb alloys and formation of InAsxSb1-x
  in Journal of electroanalytical chemistry (1992); Elsevier Sequoia, Lausanne (Svizzera)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Cattarin S.; Musiani M.M.; Casellato U.; Guerriero P.; Bertoncello R. (literal)

Pagina inizio

• 209 (literal)

Pagina fine

• 218 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://www.sciencedirect.com/science/article/pii/0022072894036042 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 380 (literal)

Rivista

• Journal of electroanalytical chemistry (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 10 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 1-2 (literal)

Note

• Scopu (literal)
• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• 1,2 : IPELP CNR, Corso Stati Uniti 4, 35020 Padova, Italy / 3,4 : ICTIMA CNR, Corso Stati Uniti 4, 35020 Padova, Italy / 5 : Dip. CIMA, via Loredan 4, 35100 Padova, Italy (literal)

Titolo

• Cathodic deposition of ternary In+As+Sb alloys and formation of InAsxSb1-x (literal)

Abstract

• In + As + Sb alloys have been deposited onto Ni and Ti cathodes from tartaric acid solutions at pH 2. Homogeneous deposits of composition suitable for achieving InAsxSb1-x can be obtained from this medium. The As-to-Sb ratio can be controlled by properly selecting solution composition and deposition potential. X-ray photoelectron spectroscopy and X-ray diffraction analyses show that formation of III-V compounds occurs at room temperature. In reacts preferentially with As rather than with Sb, but crystalline phases formed at room temperature are Sb-rich. After annealing the In + As + Sb alloys at 250 degrees C, the composition calculated from cell parameters appears similar to that measured by energy-dispersive X-ray analysis, suggesting that the entire deposit has been converted into the InAsxSb1-x crystalline phase. (literal)

Editore

• Elsevier Sequoia (Editore)

Prodotto di

• Istituto di chimica inorganica e delle superfici (ICIS) (Istituto)
• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)

Autore CNR

• SANDRO CATTARIN (Unità di personale interno)
• MARCO MUSIANI (Persona)
• UMBERTO CASELLATO (Persona)
• PAOLO GUERRIERO (Unità di personale interno)

Insieme di parole chiave

• Parole chiave di "Cathodic deposition of ternary In+As+Sb alloys and formation of InAsxSb1-x" (Insieme di parole chiave)

Incoming links:

Prodotto

• Istituto di chimica inorganica e delle superfici (ICIS) (Istituto)
• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)

Autore CNR di

• PAOLO GUERRIERO (Unità di personale interno)
• MARCO MUSIANI (Persona)
• UMBERTO CASELLATO (Persona)
• SANDRO CATTARIN (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of electroanalytical chemistry (Rivista)

Editore di

• Elsevier Sequoia (Editore)

Insieme di parole chiave di

• Parole chiave di "Cathodic deposition of ternary In+As+Sb alloys and formation of InAsxSb1-x" (Insieme di parole chiave)