Transmission electron microscopy on Hf- and Ta-carbides sintered with TaSi2 (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Transmission electron microscopy on Hf- and Ta-carbides sintered with TaSi2 (Articolo in rivista) (literal)

Anno

• 2011-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.jeurceramsoc.2011.07.003 (literal)

Alternative label

• Sciti, Diletta (1); Silvestroni, Laura (1) (2011)
  Transmission electron microscopy on Hf- and Ta-carbides sintered with TaSi2
  in Journal of the European Ceramic Society; Elsevier, Oxford (Regno Unito)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Sciti, Diletta (1); Silvestroni, Laura (1) (literal)

Pagina inizio

• 3033 (literal)

Pagina fine

• 3043 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://www.sciencedirect.com/science/article/pii/S0955221911003244 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 31 (literal)

Rivista

• Journal of the European Ceramic Society (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 11 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 15 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• (1) CNR-ISTEC, Faenza (literal)

Titolo

• Transmission electron microscopy on Hf- and Ta-carbides sintered with TaSi2 (literal)

Abstract

• The microstructure of hot pressed Hf- and Ta-carbides with 15 vol% of TaSi2 was characterized by X-ray diffraction, scanning and transmission electron microscopy in order to investigate the densification mechanisms. The microstructure of the carbides was constituted by squared grains and subgrains were recognizable only by transmission electron microscopy: the inner part was constituted by the original MC grain and the outer area by a (M,Ta)C solid solution which grew epitaxially on it. The compositional misfit and the difference of the coefficients of thermal expansion between the two regions were accommodated by 45° grain boundaries and dislocations. At the triple junctions, Ta5Si3 and Ta4.8Si3C0.3, with Hf impurities were detected. The grain boundaries were observed to be clean. The microstructure of the composites containing TaSi2 was subsequently compared to composites sintered with addition of the same amount of MoSi2 (literal)

Editore

• Elsevier (Editore)

Prodotto di

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Produzione e caratterizzazione di materiali ceramici compositi funzionali elettroconduttivi e ad alta lavorabilità. (SP.P01.033.002) (Modulo)

Autore CNR

• DILETTA SCITI (Unità di personale interno)
• LAURA SILVESTRONI (Unità di personale interno)

Insieme di parole chiave

• Keywords of "Transmission electron microscopy on Hf- and Ta-carbides sintered with TaSi2" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Produzione e caratterizzazione di materiali ceramici compositi funzionali elettroconduttivi e ad alta lavorabilità. (SP.P01.033.002) (Modulo)

Autore CNR di

• DILETTA SCITI (Unità di personale interno)
• LAURA SILVESTRONI (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of the European Ceramic Society (Rivista)

Editore di

• Elsevier (Editore)

Insieme di parole chiave di

• Keywords of "Transmission electron microscopy on Hf- and Ta-carbides sintered with TaSi2" (Insieme di parole chiave)