Corrosion protection and mechanical performance of SiO2 films deposited via PECVD on OT59 brass (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Corrosion protection and mechanical performance of SiO2 films deposited via PECVD on OT59 brass (Articolo in rivista) (literal)

Anno

• 2005-01-01T00:00:00+01:00 (literal)

Alternative label

• Moretti G. 1, Guidi F. 1, Canton R. , Battagliarin M. , G. Rossetto 2 (2005)
  Corrosion protection and mechanical performance of SiO2 films deposited via PECVD on OT59 brass
  in Anti-corrosion methods and materials
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Moretti G. 1, Guidi F. 1, Canton R. , Battagliarin M. , G. Rossetto 2 (literal)

Pagina inizio

• 266 (literal)

Pagina fine

• 275 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 5 (literal)

Rivista

• Anti-corrosion methods and materials (Rivista)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• 1. Ca’ Foscari University of Venice, Department of Chemistry 2. ICIS - CNR - Padova (literal)

Titolo

• Corrosion protection and mechanical performance of SiO2 films deposited via PECVD on OT59 brass (literal)

Abstract

• To evaluate the corrosion performance and nano-mech. behavior of a brass substrate covered by different thick SiO2 layers deposited by plasma enhanced chem. vapor deposition (PECVD) technique. The comparison between lab. and \"industrial\" objects revealed a very good corrosion behavior and good mech. performance of both of them: in particular it was possible to modulate the surface treatment to solve various problems from the industrial point of view. It was possible to reduce the Cu migration into the SiO2 coating during the PECVD deposition at a negligible level and to control it by the deposition; further, the nano-indentation tests revealed the great utility of the coating annealing in obtaining a significant improvement of the mech. properties of the coated objects. Even if some industrial problems were solved (minimization of the presence of the coating defects and transparency of the coatings), some on the layer hardness (anti-wear behavior of the industrial objects) has to be better investigated and possibly solved. The work reports a deposition process that is carried out industrially over a 2-yr period. This research reports a PECVD process realized on industrial objects: the originality is in the reached corrosion and mech. performances that made it possible to realize a satisfactory industrial deposition. (literal)

Prodotto di

• Progettazione di Nuovi Precursori Molecolari per Nanosistemi e Ottimizzazione del Processo MOCVD per la Fabbricazione e/o Modifica delle Funzionalità delle Superfici (PM.P05.001.001) (Modulo)
• Istituto di chimica inorganica e delle superfici (ICIS) (Istituto)

Autore CNR

• GILBERTO LUCIO ROSSETTO (Persona)

Insieme di parole chiave

• Keywords of "Corrosion protection and mechanical performance of SiO2 films deposited via PECVD on OT59 brass" (Insieme di parole chiave)

Incoming links:

Prodotto

• Istituto di chimica inorganica e delle superfici (ICIS) (Istituto)
• Progettazione di Nuovi Precursori Molecolari per Nanosistemi e Ottimizzazione del Processo MOCVD per la Fabbricazione e/o Modifica delle Funzionalità delle Superfici (PM.P05.001.001) (Modulo)

Autore CNR di

• GILBERTO LUCIO ROSSETTO (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Anti-corrosion methods and materials (Rivista)

Insieme di parole chiave di

• Keywords of "Corrosion protection and mechanical performance of SiO2 films deposited via PECVD on OT59 brass" (Insieme di parole chiave)