Enhanced spectroscopic properties at 1.5 mm in Er3+/Yb3+-activated silica-titania planar waveguides fabricated by rf-sputtering (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Enhanced spectroscopic properties at 1.5 mm in Er3+/Yb3+-activated silica-titania planar waveguides fabricated by rf-sputtering (Articolo in rivista) (literal)

Anno

• 2004-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/S0925-6467(03)00259-3 (literal)

Alternative label

• A. Chiasera, M. Montagna, C. Tosello, S. Pelli, G.C. Righini, M. Ferrari, L. Zampedri, A. Monteil, P. Lazzeri (2004)
  Enhanced spectroscopic properties at 1.5 mm in Er3+/Yb3+-activated silica-titania planar waveguides fabricated by rf-sputtering
  in Optical materials (Amst., Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• A. Chiasera, M. Montagna, C. Tosello, S. Pelli, G.C. Righini, M. Ferrari, L. Zampedri, A. Monteil, P. Lazzeri (literal)

Pagina inizio

• 117 (literal)

Pagina fine

• 122 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 25 (literal)

Rivista

• Optical materials (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 6 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 2 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• [ 1 ] Univ Trent, Dipartimento Fis, I-38050 Trent, Italy [ 2 ] Univ Trent, INFM, CSMFO Grp, I-38050 Trent, Italy [ 3 ] CNR, IFAC, I-50127 Florence, Italy [ 4 ] CNR, IFN, CSMFO Grp, I-38050 Trent, Italy [ 5 ] Univ Angers, CNRS, UMR 6136, Lab POMA, F-49045 Angers, France [ 6 ] IRST, ITC, I-38050 Trent, Italy (literal)

Titolo

• Enhanced spectroscopic properties at 1.5 mm in Er3+/Yb3+-activated silica-titania planar waveguides fabricated by rf-sputtering (literal)

Abstract

• Two Er3+/Yb3+-codoped 94SiO(2)-6TiO(2) planar waveguides were fabricated by the rf-sputtering technique. One sample was doped with I mol% Er and the other was also doped with ytterbium, with a molar ratio Yb/Er = 2. The thickness and the refractive index of the waveguides were measured by an m-line apparatus operating at 632.8 and 543.5 nm. The losses, for the TE0 mode, were evaluated at 632.8 and 1300 nm. The structural properties were investigated with several techniques, such as secondary ion mass spectrometry, energy dispersive spectroscopy and Raman spectroscopy. All waveguides were single-mode at 1300 and 1550 nm. An attenuation coefficient of 0.5 dB/cm at 632.8 nm and a lifetime of the I-4(13/2) metastable state of 7.2 ms were measured. Upon cw excitation at 978 nm, an increase of the 1.53 mum luminescence intensity larger than two-fold was detected in the Yb3+/Er3+-codoped waveguide with respect to the waveguide doped only with Er3+. (literal)

Prodotto di

• Sviluppo e diagnostica ottica e spettroscopica di materiali e strutture per la fotonica (MD.P03.012.001) (Modulo)
• Materiali e dispositivi attivi per le telecomunicazioni e la sensoristica (MD.P03.001.001) (Modulo)
• Institute of applied physics \"Nello Carrara\" (IFAC) (Istituto)
• Istituto di fotonica e nanotecnologie (IFN) (Istituto)

Autore CNR

• MAURIZIO FERRARI (Unità di personale interno)
• GIANCARLO RIGHINI (Unità di personale interno)
• STEFANO PELLI (Persona)
• Luca Zampedri (Persona)
• ALESSANDRO CHIASERA (Persona)

Incoming links:

Prodotto

• Istituto di fotonica e nanotecnologie (IFN) (Istituto)
• Institute of applied physics \"Nello Carrara\" (IFAC) (Istituto)
• Materiali e dispositivi attivi per le telecomunicazioni e la sensoristica (MD.P03.001.001) (Modulo)
• Sviluppo e diagnostica ottica e spettroscopica di materiali e strutture per la fotonica (MD.P03.012.001) (Modulo)

Autore CNR di

• ALESSANDRO CHIASERA (Persona)
• MAURIZIO FERRARI (Unità di personale interno)
• STEFANO PELLI (Persona)
• Luca Zampedri (Persona)
• GIANCARLO RIGHINI (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Optical materials (Rivista)