Prepeak and First Sharp Diffraction Peak in the Structure Factor of (Cs2O)(0.14)(B2O3)(0.86) Glass: Influence of Temperature (Articolo in rivista)

Type
Label
  • Prepeak and First Sharp Diffraction Peak in the Structure Factor of (Cs2O)(0.14)(B2O3)(0.86) Glass: Influence of Temperature (Articolo in rivista) (literal)
Anno
  • 2010-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1021/jp1005555 (literal)
Alternative label
  • D'Angelo, Giovanna; Crupi, Cristina; Gonzalez, Miguel Angel; Basile, Emilia; Nibali, Valeria Conti; Mondelli, Claudia (2010)
    Prepeak and First Sharp Diffraction Peak in the Structure Factor of (Cs2O)(0.14)(B2O3)(0.86) Glass: Influence of Temperature
    in The journal of physical chemistry. B
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • D'Angelo, Giovanna; Crupi, Cristina; Gonzalez, Miguel Angel; Basile, Emilia; Nibali, Valeria Conti; Mondelli, Claudia (literal)
Pagina inizio
  • 12565 (literal)
Pagina fine
  • 12571 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 114 (literal)
Rivista
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • Dipartimento di Fisica, University of Messina, Salita Sperone 31, Villaggio S. Agata, 98166 Messina, Italy, Institute Laue Langevin 6, Rue Jules Horowitz, 38042 Grenoble, France, Scuola di Specializzazione in Fisica Sanitaria, Universit√† degli Studi 'La Sapienza', Roma, Italy, Dipartimento Tecnologie e Salute, Istituto Superiore di Sanit√†, Roma, Italy, CNR-INFM OGG, Institute Laue Langevin 6, Rue Jules Horowitz, 38042 Grenoble, France (literal)
Titolo
  • Prepeak and First Sharp Diffraction Peak in the Structure Factor of (Cs2O)(0.14)(B2O3)(0.86) Glass: Influence of Temperature (literal)
Abstract
  • Neutron diffraction measurements on (Cs2O)0.14(B2O3)0.86 glass were performed at varying temperature over an extended range from room temperature to 800 K. It was found that, in the same Q range where the first sharp diffraction peak (FSDP) is observed in the static structure factor of almost all glass-forming systems, cesium borate glass shows two peaks. The intensities of these peaks increase with temperature, and their positions shift to lower Q values, in agreement with the peculiarities of the FSDP of network glasses. A description of this anomalous temperature dependence in terms of thermal relaxations of strained bonding arrangements of boron oxide units lying on the boundaries of cages present in the boron skeleton matrix is suggested. By comparing the diffraction patterns of a (Cs2O)0.14(B2O3)0.86 sample before and after a high-temperature thermal treatment with the spectra of cesium crystals, a correspondence between the medium-range structure in the glass and the related crystalline phases has been inferred. (literal)