Thermographic inspection of TBC coated gas turbine blades: Discrimination between coating over-thicknesses and adhesion defects (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Thermographic inspection of TBC coated gas turbine blades: Discrimination between coating over-thicknesses and adhesion defects (Articolo in rivista) (literal)

Anno

• 2007-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.infrared.2006.06.018 (literal)

Alternative label

• S. Marinetti; D. Robba; F. Cernuschi; P. G. Bison; E. Grinzato (2007)
  Thermographic inspection of TBC coated gas turbine blades: Discrimination between coating over-thicknesses and adhesion defects
  in Infrared physics & technology
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• S. Marinetti; D. Robba; F. Cernuschi; P. G. Bison; E. Grinzato (literal)

Pagina inizio

• 281 (literal)

Pagina fine

• 285 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 49 (literal)

Rivista

• Infrared physics & technology (Rivista)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• ITC-CNR CESI (literal)

Titolo

• Thermographic inspection of TBC coated gas turbine blades: Discrimination between coating over-thicknesses and adhesion defects (literal)

Abstract

• When performing in-field tests on thermal barrier coatings (TBCs) deposited on gas turbine blades, the main problem encountered is the difficulty to correctly interpret the experimental data. The coating thickness changes, which are not regarded as anomalies, are one of the most common sources of false alarms. They are very challenging to recognize because, unlike stains, eroded areas and optical property variations, they are not detectable in the visible band. Furthermore, their thermal signal is similar to the one produced by an adhesion defect. In this paper, a procedure to reliably discriminate thickness changes and real defects is proposed. The approach is based on the analysis of the apparent effusivity profile. Preliminary results are presented and discussed. ? 2006 Elsevier B.V. All rights reserved. (literal)

Prodotto di

• Risparmio energetico e sostenibilità ambientale di sistemi di condizionamento dell'aria e refrigerazione (SP.P04.004.001) (Modulo)

Autore CNR

• PAOLO BISON (Unità di personale interno)
• ERMANNO GRINZATO (Unità di personale interno)
• SERGIO MARINETTI (Unità di personale interno)

Insieme di parole chiave

• Parole chiave di "Thermographic inspection of TBC coated gas turbine blades: Discrimination between coating over-thicknesses and adhesion defects" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• SERGIO MARINETTI (Unità di personale interno)
• ERMANNO GRINZATO (Unità di personale interno)
• PAOLO BISON (Unità di personale interno)

Prodotto

• Risparmio energetico e sostenibilità ambientale di sistemi di condizionamento dell'aria e refrigerazione (SP.P04.004.001) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Infrared physics & technology (Rivista)

Insieme di parole chiave di

• Parole chiave di "Thermographic inspection of TBC coated gas turbine blades: Discrimination between coating over-thicknesses and adhesion defects" (Insieme di parole chiave)