Quantitative Infrared Thermographic Nondestructive Testing of Thermal Barrier Coatings (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Quantitative Infrared Thermographic Nondestructive Testing of Thermal Barrier Coatings (Articolo in rivista) (literal)

Anno

• 2003-01-01T00:00:00+01:00 (literal)

Alternative label

• Marinetti S. 1, Vavilov V. 5, Bison P. G. 2, Grinzato E. 3, Cernuschi F. 4 (2003)
  Quantitative Infrared Thermographic Nondestructive Testing of Thermal Barrier Coatings
  in Materials evaluation
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Marinetti S. 1, Vavilov V. 5, Bison P. G. 2, Grinzato E. 3, Cernuschi F. 4 (literal)

Pagina inizio

• 773 (literal)

Pagina fine

• 780 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 61/6 (literal)

Rivista

• Materials evaluation (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#descrizioneSinteticaDelProdotto

• Nella produzione di energia elettrica e nell’industria aeronautica, le barriere termiche sono largamente utilizzate per migliorare le prestazione delle turbine. In questo articolo sono analizzate le potenzialità dei test termici in questo campo di applicazione. I risultati sperimentali riportati dimostrano l’efficacia di questo metodo basato sulla stimolazione termica dell’oggetto e sull’analisi dell’evoluzione della temperatura durante il transitorio. Tale ispezione consente di individuare le aree critiche in cui il grado di adesione del rivestimento al substrato è insufficiente. (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• 1, 2, 3, 4: ITC-CNR 4: CESI, Milano 5: Tomsk Polytechnic University, Russia (literal)

Titolo

• Quantitative Infrared Thermographic Nondestructive Testing of Thermal Barrier Coatings (literal)

Abstract

• In power production and aviation, thermal barrier coatings are widely used to improve performance of turbine blades. During deposition of plasma-sprayed coatings some discontinuities might appear to affect the ability of turbine blades to withstand high temperatures and protect primary parts. Thermal testing systems are increasingly used in the testing of thermal barrier coatings due to large surface, rapid and non-contact testing capabilities. In this work, the features of the thermal nondestructive testing (NDT) of thermal barrier coatings are summarized and the current problems, such as residual heating, spurious reflections and coating transparency, are addressed. The experimental data are presented along with advanced processing results obtained by using pulse phase thermography and principal component analysis. The comparison of the processing techniques is done in the detection of delaminations between the coating and substrate. The problem of the discrimination between the coating thickness variations and delaminations, as well as the sensitivity of thermal NDT, is discussed. (literal)

Autore CNR

• PAOLO BISON (Unità di personale interno)
• SERGIO MARINETTI (Unità di personale interno)
• ERMANNO GRINZATO (Unità di personale interno)

Insieme di parole chiave

• Keywords of "Quantitative Infrared Thermographic Nondestructive Testing of Thermal Barrier Coatings" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• SERGIO MARINETTI (Unità di personale interno)
• ERMANNO GRINZATO (Unità di personale interno)
• PAOLO BISON (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Materials evaluation (Rivista)

Insieme di parole chiave di

• Keywords of "Quantitative Infrared Thermographic Nondestructive Testing of Thermal Barrier Coatings" (Insieme di parole chiave)