General Strategy for Direct Synthesis of L10 Nanoparticle Alloys from Layered Precursor: The Case of FePt (Articolo in rivista)
- Type
- Label
- General Strategy for Direct Synthesis of L10 Nanoparticle Alloys from Layered Precursor: The Case of FePt (Articolo in rivista) (literal)
- Anno
- 2009-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1021/cm9003992 (literal)
- Alternative label
Capobianchi A. (1), Colapietro M. (2), Fiorani D. (1), Foglia S. (3), Imperatori P. (1), Laureti S. (1), Palange E.(4) (2009)
General Strategy for Direct Synthesis of L10 Nanoparticle Alloys from Layered Precursor: The Case of FePt
in Chemistry of materials
(literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- Capobianchi A. (1), Colapietro M. (2), Fiorani D. (1), Foglia S. (3), Imperatori P. (1), Laureti S. (1), Palange E.(4) (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#note
- http://dx.doi.org/10.1021/cm9003992 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
- Note
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- 1) Istituto di Struttura della Materia-CNR, Via Salaria Km 29.300, Montelibretti, 00016 Rome, Italy,;
2) Istituto di Fotonica e Nanotecnologie-CNR Via Cineto Romano 42, Rome, Italy;
3) Dipartimento di Chimica, Università degli Studi di Roma La Sapienza P.le A. Moro, 00185 Rome, Italy;
4) Dipartimento di Ingegneria Elettrica e dellInformazione, Università degli Studi dell'Aquila, Monteluco di Roio, 67040 L'Aquila, Italy (literal)
- Titolo
- General Strategy for Direct Synthesis of L10 Nanoparticle Alloys from Layered Precursor: The Case of FePt (literal)
- Abstract
- A general thermal decomposition strategy for the synthesis of highly chemically ordered L10 alloy nanoparticles is presented. L10 FePt nanoparticles with an average diameter of 5 nm were obtained directly from the atomically layered precursor FePtCl6_6H2O. The method is easy and low cost, and the FePt nanoparticles, obtained at 400C have a high magnetic anisotropy. (literal)