Versatile Synthesis of Carbon-rich LiFePO4 Enhancing Its Electrochemical Properties (Articolo in rivista)
- Type
- Label
- Versatile Synthesis of Carbon-rich LiFePO4 Enhancing Its Electrochemical Properties (Articolo in rivista) (literal)
- Anno
- 2004-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1149/1.1651393 (literal)
- Alternative label
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- Bauer E.M. (a); Bellitto C. (a); Pasquali M.(b); Prosini P.P. (c); Righini G. (a) (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#note
- http://dx.doi.org/10.1149/1.1651393 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
- Note
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- a) CNR, Istituto di Struttura della Materia,, I-00016 Monterotondo Scalo, Roma, Italy;
b) Dipartimento ICMMPM, Facoltà di Ingegneria, Università di Roma \"La Sapienza\", Roma, Italy;
c) ENEA, Idrocomb, CR Casaccia, Roma 00060, Italy (literal)
- Titolo
- Versatile Synthesis of Carbon-rich LiFePO4 Enhancing Its Electrochemical Properties (literal)
- Abstract
- LiFePO4/C composites were prepared from thermal decomposition of Fe(II) organophosphonates Fe[(RPO3)(H2O)] (R = methyl or phenyl group! in the presence of Li2CO3 at high temperature and under inert atmosphere. The compounds were characterized by chemical analysis, thermogravimetric analysis and differential scanning colorimetry, X-ray powder diffraction, and scanning electron microscopy. Electrodes were fabricated for the electrochemical characterization. The cathode material obtained from Fe[C6H5PO3(H2O)] showed a specific energy evaluated at C/10 rate of about 550 Wh kg(-1). The specific power calculated at 30C rate in excess at 14,000 W kg(-1), while the specific energy was about 28% of the theoretical one. No capacity fading was observed upon cycling. (literal)