Thermally-induced morphological transition in WOx deposited on a ZrO2(100) substrate (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Thermally-induced morphological transition in WOx deposited on a ZrO2(100) substrate (Articolo in rivista) (literal)

Anno

• 2007-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.susc.2007.01.002 (literal)

Alternative label

• Colonna S., Pompeo G., Girasole M., Gazzoli D., Pettiti I., Valigi M. (2007)
  Thermally-induced morphological transition in WOx deposited on a ZrO2(100) substrate
  in Surface science
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Colonna S., Pompeo G., Girasole M., Gazzoli D., Pettiti I., Valigi M. (literal)

Pagina inizio

• 1389 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 601 (literal)

Rivista

• Surface science (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 5 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• CNR Istituto di Struttura della Materia; CNR Istituto di Struttura della Materia; CNR Istituto di Struttura della Materia; Dipartimento di Chimica, Università di Roma “La Sapienza”, Roma, Italy; Dipartimento di Chimica, Università di Roma “La Sapienza”, Roma, Italy; Dipartimento di Chimica, Università di Roma “La Sapienza”, Roma, Italy (literal)

Titolo

• Thermally-induced morphological transition in WOx deposited on a ZrO2(100) substrate (literal)

Abstract

• A combined atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS) study of tungsten oxide model catalysts is presented. The model catalysts were prepared by applying the real preparation method to a ZrO2(1 0 0) single crystal support. AFM imaged several granular structures of scattered dimensions on the surface of ZrO2(1 0 0) in the as prepared samples. After heating, at low loading the tungsten species rearranged into small WOx particles strongly interacting with the substrate. At high tungsten content large WO3 aggregates also formed. XPS analysis confirmed these changes. The estimated surface density of the interacting W-containing species closely matched that of real catalysts. (literal)

Prodotto di

• Institute of structure of matter (ISM) (Istituto)
• Microscopia a Scansione a Sonda Locale su sistemi nanostrutturati e materiali biologici (MD.P06.006.001) (Modulo)

Autore CNR

• GIULIANO POMPEO (Unità di personale esterno)
• STEFANO COLONNA (Persona)
• MARCO GIRASOLE (Unità di personale interno)

Incoming links:

Autore CNR di

• STEFANO COLONNA (Persona)
• MARCO GIRASOLE (Unità di personale interno)
• GIULIANO POMPEO (Unità di personale esterno)

Prodotto

• Institute of structure of matter (ISM) (Istituto)
• Microscopia a Scansione a Sonda Locale su sistemi nanostrutturati e materiali biologici (MD.P06.006.001) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Surface science (Rivista)