Sol-gel combustion synthesis of BNBT powders (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Sol-gel combustion synthesis of BNBT powders (Articolo in rivista) (literal)

Anno

• 2008-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1007/s10971-008-1693-4 (literal)

Alternative label

• Elisa Mercadelli ; Carmen Galassi ; Anna Luisa Costa ; Stefania Albonetti; Alessandra Sanson (2008)
  Sol-gel combustion synthesis of BNBT powders
  in Journal of sol-gel science and technology
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Elisa Mercadelli ; Carmen Galassi ; Anna Luisa Costa ; Stefania Albonetti; Alessandra Sanson (literal)

Pagina inizio

• 39 (literal)

Pagina fine

• 45 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://www.springerlink.com/content/453121p6v610wp22/fulltext.html (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 46 (literal)

Rivista

• Journal of sol-gel science and technology (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#note

• In: Journal of Sol-Gel Science and Technology, vol. 46 (1) pp. 39 - 45. Springer, 2008. (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 1 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Albonetti: Univ Bologna, Dept Ind Chem & Mat, Bologna, Italy Mercadelli Galassi, Costa, Sanson: CNR-ISTEC, Faenza (literal)

Titolo

• Sol-gel combustion synthesis of BNBT powders (literal)

Abstract

• Ba-modified bismuth sodium titanate with composition 0.94[(Bi0.5Na0.5)TiO3]-0.06BaTiO3 (BNBT) was prepared by a citrate nitrate sol-gel combustion method. The sol was obtained using barium acetate, bismuth nitrate, sodium nitrate and a peroxo-citrate complex of titanium isopropoxide as starting precursors. Various molar ratios of citrate/nitrate (C/N) were considered for the sol production. The corresponding gels were fired at different temperatures (300, 400, 500°C) in order to evaluate the conditions necessary to obtain the decomposition of the precursors and the formation of the pure BNBT perovskitic phase in a single step. The best conditions to obtain the desired phase are: (C/N) = 0.2, and combustion temperature of 500°C. Ball milled powders were densified at a temperature 100°C lower than the one generally used for powder produced with the conventional mixed oxide route. The electrical properties are comparable to those reported for conventionally prepared materials. (literal)

Prodotto di

• Processi e materiali per applicazioni elettromeccaniche (SP.P02.009.001) (Modulo)
• Institute of science and technology for ceramics (ISTEC) (Istituto)

Autore CNR

• ELISA MERCADELLI (Persona)
• ALESSANDRA SANSON (Unità di personale interno)
• CARMEN GALASSI (Unità di personale interno)
• ANNA LUISA COSTA (Persona)

Insieme di parole chiave

• Parole chiave di "Sol-gel combustion synthesis of BNBT powders" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Processi e materiali per applicazioni elettromeccaniche (SP.P02.009.001) (Modulo)

Autore CNR di

• CARMEN GALASSI (Unità di personale interno)
• ALESSANDRA SANSON (Unità di personale interno)
• ELISA MERCADELLI (Persona)
• ANNA LUISA COSTA (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of sol-gel science and technology (Rivista)

Insieme di parole chiave di

• Parole chiave di "Sol-gel combustion synthesis of BNBT powders" (Insieme di parole chiave)