Spark plasma sintering of ultrarefractory compounds (Articolo in rivista)

Type
Label
  • Spark plasma sintering of ultrarefractory compounds (Articolo in rivista) (literal)
Anno
  • 2008-01-01T00:00:00+01:00 (literal)
Alternative label
  • Sciti D.; Nygren M. (2008)
    Spark plasma sintering of ultrarefractory compounds
    in Journal of materials science
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Sciti D.; Nygren M. (literal)
Pagina inizio
  • 6414 (literal)
Pagina fine
  • 6421 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 43 (literal)
Rivista
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • CNR-ISTEC, Faenza, Arrhenius Laboratory, Department of Inorganic Chemistry, Stockolm University, Stockolm, Sweden (literal)
Titolo
  • Spark plasma sintering of ultrarefractory compounds (literal)
Abstract
  • Spark plasma sintering experiments were conducted on Zr- and Hf- based borides and carbides with addition of 1, 3, and 9 Vol% MoSi2 as sintering aid. For comparison, as-received ZrC, HfC, ZrB2, HfB2 powders were also sintered. The microstructural features were investigated by means of SEM-EDS technique. Silicon carbide was detected in all the doped compositions along with significant amounts of oxide species (Hf/ZrO2, and SiO2). The effect of the MoSi2 content on densification, microstructure and mechanical properties is analysed. (literal)
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Prodotto
Autore CNR di
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Insieme di parole chiave di
data.CNR.it