On the toughening mechanisms of MoSi2 reinforced Si3N4 ceramics (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• On the toughening mechanisms of MoSi2 reinforced Si3N4 ceramics (Articolo in rivista) (literal)

Anno

• 2007-01-01T00:00:00+01:00 (literal)

Alternative label

• D.Sciti, G. Celotti, G. Pezzotti, S. Guicciardi (2007)
  On the toughening mechanisms of MoSi2 reinforced Si3N4 ceramics
  in Applied physics. A, Materials science & processing (Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• D.Sciti, G. Celotti, G. Pezzotti, S. Guicciardi (literal)

Pagina inizio

• 243 (literal)

Pagina fine

• 248 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 86 (literal)

Rivista

• Applied physics. A, Materials science & processing (Rivista)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• D. Sciti, G. Celotti, S. Guicciardi, ISTEC-CNR, G. Pezzotti, Research Institute for Nanoscience (RIN), Kyoto Institute of Technology, Sakyo-ku, Matsugasaki, 606-8585 Kyoto, Japan (literal)

Titolo

• On the toughening mechanisms of MoSi2 reinforced Si3N4 ceramics (literal)

Abstract

• The toughness increment occurring in Si3N4-based composites due to the addition of MoSi2 particles was compared to the predictions of theoretical models based on the combination of residual stresses and crack deflection toughening mechanisms. A direct application of theoretical models led to a substantial discrepancy between predicted and observed values. For this reason, the basic parameters of the theoretical models were experimentally evaluated. The residual stresses were assessed by measuring the strain in the reinforcing particles by X-ray diffraction. Moreover, the MoSi2 interparticle distance was calculated by image analysis and the crack paths were analyzed in order to check the actual extent of crack deflection. The overall toughness increase recalculated as the sum of the newly estimated values of residual stresses and crack deflection contributions, was shown to be in good agreement with the experimental results. (literal)

Prodotto di

• Produzione e caratterizzazione di materiali ceramici compositi funzionali elettroconduttivi e ad alta lavorabilità. (SP.P01.033.002) (Modulo)
• Institute of science and technology for ceramics (ISTEC) (Istituto)

Autore CNR

• STEFANO GUICCIARDI O GUIZZARDI (Persona)
• GIANCARLO CELOTTI (Unità di personale interno)
• DILETTA SCITI (Unità di personale interno)

Insieme di parole chiave

• Parole chiave di "On the toughening mechanisms of MoSi2 reinforced Si3N4 ceramics" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Produzione e caratterizzazione di materiali ceramici compositi funzionali elettroconduttivi e ad alta lavorabilità. (SP.P01.033.002) (Modulo)

Autore CNR di

• DILETTA SCITI (Unità di personale interno)
• STEFANO GUICCIARDI O GUIZZARDI (Persona)
• GIANCARLO CELOTTI (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Applied physics. A, Materials science & processing (Rivista)

Insieme di parole chiave di

• Parole chiave di "On the toughening mechanisms of MoSi2 reinforced Si3N4 ceramics" (Insieme di parole chiave)