Joining ZrB2-SiC composites using glass interlayers (Articolo in rivista)
- Type
- Label
- Joining ZrB2-SiC composites using glass interlayers (Articolo in rivista) (literal)
- Anno
- 2005-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1007/s10853-005-2813-y (literal)
- Alternative label
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- Laura Esposito, Alida Bellosi (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url
- http://www.springerlink.com/content/w34t302122r28884/ (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
- Note
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- Titolo
- Joining ZrB2-SiC composites using glass interlayers (literal)
- Abstract
- A joining technique, based on the use of a glass powder as a bonding interlayer between
two ceramic pieces, is tested for a ZrB2-SiC composite. At the bonding temperature, the
glass melts, wets the ceramic and flows through the interface driven by the capillary
pressure that builds up between the two contacting ceramic surfaces, promoting their
adhesion. The behaviour of three glasses is compared: two in the system Ca-Al-Si-O
(melting temperatures 1400 and 1210.C) and one in the system Y-Al-Si-O (melting
temperature 1440.C). The ceramic-glass interfacial characteristics depend mainly on the
temperature, on the composition of the glass and on the phenomena influencing the
adhesion, such as the partial dissolution of the ceramic grains when the glass wets them.
The 3-point flexural strength values of the joints obtained by the system that resulted with
the more homogeneous interface are also reported. (literal)
- Prodotto di
- Autore CNR
- Insieme di parole chiave
Incoming links:
- Prodotto
- Autore CNR di
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
- Insieme di parole chiave di