Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex situ tapes (Articolo in rivista)

Type
Label
  • Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex situ tapes (Articolo in rivista) (literal)
Anno
  • 2008-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1063/1.3021468 (literal)
Alternative label
  • Malagoli, A; Braccini, V; Tropeano, M; Vignolo, M; Bernini, C; Fanciulli, C; Romano, G; Putti, M; Ferdeghini, C; Mossang, E; Polyanskii, A; Larbalestier, DC (2008)
    Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex situ tapes
    in Journal of applied physics
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Malagoli, A; Braccini, V; Tropeano, M; Vignolo, M; Bernini, C; Fanciulli, C; Romano, G; Putti, M; Ferdeghini, C; Mossang, E; Polyanskii, A; Larbalestier, DC (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 104 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 10 (literal)
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • \"[Malagoli, A.; Braccini, V.; Tropeano, M.; Vignolo, M.; Bernini, C.; Fanciulli, C.; Romano, G.; Putti, M.; Ferdeghini, C.] CNR INFM LAMIA, I-16152 Genoa, Italy; [Mossang, E.] CNRS, Grenoble High Magnet Field Lab, F-38042 Grenoble 9, France; [Polyanskii, A.; Larbalestier, D. C.] Florida State Univ, Natl High Magnet Field Lab, Tallahassee, FL 32310 USA (literal)
Titolo
  • Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex situ tapes (literal)
Abstract
  • Ex situ powder-in-tube MgB2 tapes prepared with ball-milled, undoped powders showed a strong enhancement of the irreversibility field H-*, the upper critical field H-c2, and the critical current density J(c)(H) together with the suppression of the anisotropy of all of these quantities. J(c) reached 10(4) A/cm(2) at 4.2 K and 10 T, with an irreversibility field of about 14 T at 4.2 K, and H-c2 of 9 T at 25 K, high values for not-doped MgB2. The enhanced J(c) and H-* values are associated with significant grain refinement produced by milling of the MgB2 powder, which enhances grain boundary pinning, even if at the same time also reducing the connectivity from about 12% to 8%. Although enhanced pinning and diminished connectivity are in opposition, the overall influence of ball milling on J(c) is positive because the increased density of grains with a size comparable with the mean free path produces strong electron scattering that substantially increases H-c2, especially H-c2 perpendicular to the Mg and B planes. (literal)
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Autore CNR di
Prodotto
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Insieme di parole chiave di
data.CNR.it