A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 Nanotube Arrays (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 Nanotube Arrays (Articolo in rivista) (literal)

Anno

• 2009-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1166/nnl.2009.1020 (literal)

Alternative label

• L. M. S. Perdicaro; R. G. Toro; M. E. Fragalà; G. Malandrino; R. Lo Nigro; C. Bongiorno; M. Losurdo; M. M. Giangregorio; G. Bruno (2009)
  A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 Nanotube Arrays
  in Nanoscience and nanotechnology letters (Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• L. M. S. Perdicaro; R. G. Toro; M. E. Fragalà; G. Malandrino; R. Lo Nigro; C. Bongiorno; M. Losurdo; M. M. Giangregorio; G. Bruno (literal)

Pagina inizio

• 87 (literal)

Pagina fine

• 92 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 1 (literal)

Rivista

• Nanoscience and nanotechnology letters (Rivista)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• [ 1 ] Univ Catania, Dipartimento Sci Chim, ISTM CNR, I-95125 Catania, Italy [ 2 ] INSTM UdR Catania, I-95125 Catania, Italy [ 3 ] CNR, IMM, I-95121 Catania, Italy [ 4 ] CNR, IMIP, I-70126 Bari, Italy [ 5 ] UdR Bari, INSTM, I-70126 Bari, Italy (literal)

Titolo

• A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 Nanotube Arrays (literal)

Abstract

• Large area Co3O4 nanotube arrays were fabricated through a metal-organic chemical vapour deposition (MOCVD) template route using the Co(tta)(2)center dot tmeda (Htta = 2 thenoyl-trifluoroacetone, tmeda = N,N,N,N'-tetramethylethylendiamine) as precursor and anodic aluminum oxide (AAO) as template. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) indicated a very uniform distribution of nanotubes forming an array on a very large scale of the order of mm(2). X-ray diffraction (XRD) pattern shows the formation of the Co3O4 cubic spinel phase. The electron diffraction confirmed the crystalline Co3O4 phase even after removal of the MO template. Spectroscopic ellipsometry was used to measure the optical properties of nanotubes and to discuss the effect of the nanostructure with respect to the optical properties of Co3O4 thin films. (literal)

Prodotto di

• Istituto di Nanotecnologia (NANOTEC) (Istituto)
• Plasmi per la Scienza dei Materiali (MD.P03.025.001) (Modulo)

Autore CNR

• CORRADO BONGIORNO (Unità di personale interno)
• GIOVANNI BRUNO (Unità di personale interno)
• RAFFAELLA LO NIGRO (Unità di personale interno)
• MARIA MICHELA GIANGREGORIO (Persona)
• ROBERTA GRAZIA TORO (Unità di personale interno)
• MARIA LOSURDO (Unità di personale interno)

Incoming links:

Prodotto

• Istituto di Nanotecnologia (NANOTEC) (Istituto)
• Plasmi per la Scienza dei Materiali (MD.P03.025.001) (Modulo)

Autore CNR di

• GIOVANNI BRUNO (Unità di personale interno)
• MARIA LOSURDO (Unità di personale interno)
• RAFFAELLA LO NIGRO (Unità di personale interno)
• CORRADO BONGIORNO (Unità di personale interno)
• MARIA MICHELA GIANGREGORIO (Persona)
• ROBERTA GRAZIA TORO (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Nanoscience and nanotechnology letters (Rivista)