Magnetic anisotropy and magnetisation processes in 3:29, 1:12 and 2:17 type Nd:(Fe, Co, Ti) related compounds (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Magnetic anisotropy and magnetisation processes in 3:29, 1:12 and 2:17 type Nd:(Fe, Co, Ti) related compounds (Articolo in rivista) (literal)

Anno

• 2004-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/S0304-8853(03)00618-8 (literal)

Alternative label

• Negri D.; Paoluzi A.; Pareti L. (2004)
  Magnetic anisotropy and magnetisation processes in 3:29, 1:12 and 2:17 type Nd:(Fe, Co, Ti) related compounds
  in Journal of magnetism and magnetic materials; Elsevier, Amsterdam (Paesi Bassi)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Negri D.; Paoluzi A.; Pareti L. (literal)

Pagina inizio

• 302 (literal)

Pagina fine

• 310 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://www.sciencedirect.com/science/article/pii/S0304885303006188 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 269 (literal)

Rivista

• Journal of magnetism and magnetic materials (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 9 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 3 (literal)

Note

• Scopu (literal)
• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• a Istituto IMEM del Consiglio Nazionale delle Ricerche, Parco Area delle Scienze 37/A, Parma 43010, Italy (literal)

Titolo

• Magnetic anisotropy and magnetisation processes in 3:29, 1:12 and 2:17 type Nd:(Fe, Co, Ti) related compounds (literal)

Abstract

• A study of the composition and temperature dependence of the magnetocrystalline anisotropy has been performed in the pseudo-ternary system Nd3(Fe1-xCox)29-yTiy (x = 0, 0.1, 0.3, 0.5, 0.7, 1.0 and y = 1:5) and in the corresponding compositions 2:17 and 1:12 related phases. The occurrence of field induced transitions, which were identified as firstorder magnetisation process, was observed in all the phases. In most of the samples the transitions still persist at room temperature. It has been found that the definition of easy and hard directions in the 3:29 phase results from the combined anisotropy contributions of the 1:12 and 2:17 constituent blocks. The additivity of the anisotropy contributions is accomplished only qualitatively. (literal)

Editore

• Elsevier (Editore)

Prodotto di

• Istituto dei materiali per l'elettronica ed il magnetismo (IMEM) (Istituto)
• Progettazione, preparazione e studio di materiali magnetici funzionali (MD.P04.002.001) (Modulo)

Autore CNR

• LUIGI PARETI (Unità di personale interno)
• ANTONIO ERMANNO PAOLUZI (Persona)

Insieme di parole chiave

• Keywords of "Magnetic anisotropy and magnetisation processes in 3:29, 1:12 and 2:17 type Nd:(Fe, Co, Ti) related compounds" (Insieme di parole chiave)

Incoming links:

Prodotto

• Istituto dei materiali per l'elettronica ed il magnetismo (IMEM) (Istituto)
• Progettazione, preparazione e studio di materiali magnetici funzionali (MD.P04.002.001) (Modulo)

Autore CNR di

• LUIGI PARETI (Unità di personale interno)
• ANTONIO ERMANNO PAOLUZI (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of magnetism and magnetic materials (Rivista)

Editore di

• Elsevier (Editore)

Insieme di parole chiave di

• Keywords of "Magnetic anisotropy and magnetisation processes in 3:29, 1:12 and 2:17 type Nd:(Fe, Co, Ti) related compounds" (Insieme di parole chiave)