Perpendicular magnetic anisotropy and stripe domains in ultrathin Co/Au sputtered multilayers (Articolo in rivista)

Type

Label

Perpendicular magnetic anisotropy and stripe domains in ultrathin Co/Au sputtered multilayers (Articolo in rivista) (literal)

Anno

Alternative label

Donzelli O., Palmeri D., Musa L., Casoli F., Albertini F., Pareti L., Turilli G. (2003)
Perpendicular magnetic anisotropy and stripe domains in ultrathin Co/Au sputtered multilayers
in Journal of applied physics
(literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

Donzelli O., Palmeri D., Musa L., Casoli F., Albertini F., Pareti L., Turilli G. (literal)

Pagina inizio

Pagina fine

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

Rivista

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#descrizioneSinteticaDelProdotto

La conoscenza del campo di anisotropia è un parametro importante per definire i limiti di impiego dei materiali magnetici, in particolare in applicazioni come magneti permanenti e registrazione magnetica. La possibilità di una rapida e affidabile determinazione di questa grandezza è quindi di notevole interesse. Mediante il confronto fra misure magnetometriche ed osservazioni al microscopio a forza magnetica su multistrati Co/Au ad anisotropia perpendicolare, applicando il modello di Draaisma e de Jonge sui domini a strisce, è stato messo a punto un metodo (di facile applicazione) che permette di determinare le costanti di anisotropia effettive di sistemi planari, a partire dalla larghezza dei domini magnetici. (literal)

Note

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

1-2 Università di Ferrara; 3 Crys-Tel Communications, Bologna; 4 IMEM-CNR, Parma; (literal)

Titolo

Perpendicular magnetic anisotropy and stripe domains in ultrathin Co/Au sputtered multilayers (literal)

Abstract

Magnetometric and magnetic force microscopy (MFM) measurements were performed on [Co(6 Å)/Au(27 Å)]27 multilayers grown at different sputtering pressures (0.89 Pa). All the as-prepared samples display perpendicular magnetic anisotropy that has its maximum value at intermediate pressures, while a monotonic decrease of the saturation magnetization was found with increasing pressure. As found by MFM, a relevant characteristic of these systems is the magnetic stripe domain structure. The application of the stripe domain model of Draaisma and de Jonge [H. J. G. Draaisma and W. J. M. de Jonge, J. Appl. Phys. 62, 3318 (1987)] allows us to satisfactorily reproduce the magnetization processes and to determine the anisotropy constants (Keff) starting from the domain width. The obtained Keff values display the same behavior and order of magnitude as those deduced from the area enclosed between parallel and perpendicular magnetization curves. The measurement of the stripe domain size with MFM thus results in an easy and reliable method for the evaluation of the anisotropy constants in multilayers with perpendicular anisotropy. ©2003 American Institute of Physics. (literal)