Thermally induced self-assembly of cylindrical nanodomains in low molecular weight PS-b-PMMA thin films (Articolo in rivista)

Type
Label
  • Thermally induced self-assembly of cylindrical nanodomains in low molecular weight PS-b-PMMA thin films (Articolo in rivista) (literal)
Anno
  • 2014-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1088/0957-4484/25/4/045301 (literal)
Alternative label
  • Seguini, Gabriele; Giammaria, Tommaso J.; Ferrarese Lupi, Federico; Sparnacci, Katia; Antonioli, Diego; Gianotti, Valentina; Vita, Francesco; Placentino, Immacolata F.; Hilhorst, Jan; Ferrero, Claudio; Francescangeli, Oriano; Laus, Michele; Perego, Michele (2014)
    Thermally induced self-assembly of cylindrical nanodomains in low molecular weight PS-b-PMMA thin films
    in Nanotechnology (Bristol. Print)
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Seguini, Gabriele; Giammaria, Tommaso J.; Ferrarese Lupi, Federico; Sparnacci, Katia; Antonioli, Diego; Gianotti, Valentina; Vita, Francesco; Placentino, Immacolata F.; Hilhorst, Jan; Ferrero, Claudio; Francescangeli, Oriano; Laus, Michele; Perego, Michele (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 25 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
  • 6 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 4 (literal)
Note
  • ISI Web of Science (WoS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • Consiglio Nazionale delle Ricerche (CNR); University of Eastern Piedmont Amedeo Avogadro; Marche Polytechnic University; Marche Polytechnic University; European Synchrotron Radiat Facil (literal)
Titolo
  • Thermally induced self-assembly of cylindrical nanodomains in low molecular weight PS-b-PMMA thin films (literal)
Abstract
  • The phase behaviour in thin films of an asymmetric polystyrene-b-polymethylmethacrylate (PS-b-PMMA) block copolymer with a molecular weight of 39 kg mol 1 was assessed at a wide range of temperatures and times. Cylindrical PMMA structures featuring a diameter close to 10 nm and perpendicularly oriented with respect to the substrate were obtained at 180 degrees C in relatively short annealing times (t <= 30 min) by means of a simple thermal treatment performed in a standard rapid thermal processing machine. (literal)
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Prodotto
Autore CNR di
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Insieme di parole chiave di
data.CNR.it