Liquid crystalline elastomers based on diglycidyl terminated monomers and aliphatic acids. Part 2: mechanical characterization (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Liquid crystalline elastomers based on diglycidyl terminated monomers and aliphatic acids. Part 2: mechanical characterization (Articolo in rivista) (literal)

Anno

• 2005-01-01T00:00:00+01:00 (literal)

Alternative label

• M. Giamberini, P. Cerruti, V. Ambrogi, C. Vestito, F. Covino, C. Carfagna (2005)
  Liquid crystalline elastomers based on diglycidyl terminated monomers and aliphatic acids. Part 2: mechanical characterization
  in Polymer (Guildford)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• M. Giamberini, P. Cerruti, V. Ambrogi, C. Vestito, F. Covino, C. Carfagna (literal)

Pagina inizio

• 9113 (literal)

Pagina fine

• 9125 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 46 (literal)

Rivista

• Polymer (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#note

• 4 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• 2,3,4,5,6 Dipartimento di Ingegneria dei Materiali e della Produzione, Universita' degli Studi di Napoli \"Federico II\" (literal)

Titolo

• Liquid crystalline elastomers based on diglycidyl terminated monomers and aliphatic acids. Part 2: mechanical characterization (literal)

Abstract

• In this paper the orientational behaviour and the mechanical properties of four LC elastomers, obtained by reacting two mesogenic epoxy monomers, DOMS and PHBHQ, with two aliphatic acids having four (AA) and eight (SA) methylene groups, respectively, have been studied. Stress-relaxation experiments performed at a strain value ƒÕ = 0.2 showed shorter relaxation times and lower relaxation moduli for AA-based elastomers as compared with the PHBHQ-SA system. Stress-strain curves of the LC elastomers showed the plateau attributed to the soft elasticity. The lower crosslink density in the case of DOMS-based elastomers affected the tensile properties adversely. Moreover, PHBHQ-SA was found to show poor strain recovery and it recovered the original size only upon heating to isotropic phase. This evidence was also confirmed by isostrain measurements. Dynamic-mechanical thermal analysis (DMTA) confirmed the existence of a heterogeneous, more branched structure in the case of DOMS-based systems. The particular features of the DMTA response strongly depend on the material composition and, in general, were found in agreement with other evidences from the literature. (literal)

Prodotto di

• Polimeri, compositi e nanostrutture con proprietà funzionali programmate (PM.P02.003.001) (Modulo)
• Institute for composite and biomedical materials (IMCB) (Istituto)

Autore CNR

• MARTA GIAMBERINI (Persona)

Insieme di parole chiave

• Parole chiave di "Liquid crystalline elastomers based on diglycidyl terminated monomers and aliphatic acids. Part 2: mechanical characterization" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute for composite and biomedical materials (IMCB) (Istituto)
• Polimeri, compositi e nanostrutture con proprietà funzionali programmate (PM.P02.003.001) (Modulo)

Autore CNR di

• MARTA GIAMBERINI (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Polymer (Rivista)

Insieme di parole chiave di

• Parole chiave di "Liquid crystalline elastomers based on diglycidyl terminated monomers and aliphatic acids. Part 2: mechanical characterization" (Insieme di parole chiave)