Deposition and electrochemical characterization of Yttrium doped Barium cerate and zirconate heterostructures (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Deposition and electrochemical characterization of Yttrium doped Barium cerate and zirconate heterostructures (Articolo in rivista) (literal)

Anno

• 2014-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.tsf.2014.04.073 (literal)

Alternative label

• Yang, N.; Tebano, A.; Di Castro, D.; Balestrino, G.; D'Epifanio, A.; Licoccia, S.; Di Bartolomeo, E. (2014)
  Deposition and electrochemical characterization of Yttrium doped Barium cerate and zirconate heterostructures
  in Thin solid films (Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Yang, N.; Tebano, A.; Di Castro, D.; Balestrino, G.; D'Epifanio, A.; Licoccia, S.; Di Bartolomeo, E. (literal)

Pagina inizio

• 264 (literal)

Pagina fine

• 268 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 562 (literal)

Rivista

• Thin solid films (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 5 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• University of Rome Tor Vergata; University of Rome Tor Vergata; Consiglio Nazionale delle Ricerche (CNR); University of Rome Tor Vergata (literal)

Titolo

• Deposition and electrochemical characterization of Yttrium doped Barium cerate and zirconate heterostructures (literal)

Abstract

• Epitaxial heterostructures consisting of an yttrium doped barium cerate, BaCe0.8Y0.2O3,(BCY) layer sandwiched between two yttrium doped barium zirconate, BaZr0.8Y0.2O3,(BZY) thin layers have been deposited on insulating (001) MgO substrates by pulsed laser deposition. The first BZY layer was aimed at improving the lattice match with the MgO substrate, the second at protecting the BCY layer. Ionic conductivity has been studied in the 300 degrees C-600 degrees C temperature range as a function of the BCY thickness in dry air and wet 5% H-2 in Ar atmosphere. In both atmospheres, heterostructures showed a conductivity slightly larger than that of BCY pellets sintered under optimized conditions. Such a result has been attributed to the absence of blocking grain boundaries in the epitaxial heterostructures due to their good crystallographic quality. The BCY sandwich heterostructures showed an improved chemical stability relative to standard BCY pellets. (C) 2014 Elsevier B.V. All rights reserved. (literal)

Prodotto di

• Proprietà fondamentali di materiali funzionali e applicazioni per l'energetica (MD.P04.026.002) (Modulo)
• Crescita e caratterizzazioni magnetiche, ottiche e di trasporto di film e multistrati epitassiali o nanostrutturati (MD.P04.025.002) (Modulo)

Autore CNR

• Giuseppe Balestrino (Persona)
• ANTONELLO TEBANO (Persona)
• DANIELE DI CASTRO (Persona)

Insieme di parole chiave

• Parole chiave di "Deposition and electrochemical characterization of Yttrium doped Barium cerate and zirconate heterostructures" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• Giuseppe Balestrino (Persona)
• ANTONELLO TEBANO (Persona)
• DANIELE DI CASTRO (Persona)
• http://www.cnr.it/ontology/cnr/individuo/unitaDiPersonaleEsterno/ID24523

Prodotto

• Crescita e caratterizzazioni magnetiche, ottiche e di trasporto di film e multistrati epitassiali o nanostrutturati (MD.P04.025.002) (Modulo)
• Proprietà fondamentali di materiali funzionali e applicazioni per l'energetica (MD.P04.026.002) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Thin solid films (Rivista)

Insieme di parole chiave di

• Parole chiave di "Deposition and electrochemical characterization of Yttrium doped Barium cerate and zirconate heterostructures" (Insieme di parole chiave)