Quaternized Xylan and sulfate films (Articolo in rivista)
- Type
- Label
- Quaternized Xylan and sulfate films (Articolo in rivista) (literal)
- Anno
- 2014-01-01T00:00:00+01:00 (literal)
- Alternative label
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- Simkovic I.; Tracz A.; Kelnar I.; Uhliarikova I.; Mendichi R. (literal)
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- Mendichi R.; Istituto per lo Studio delle Macromolecole (CNR), Milano, Italy
Simkovic I., Uhliarikova I.; Institute of Chemistry, Slovak Academy of Sciences, Bratislava, Slovakia
Tracz A.; Centre of Molecular and Macromolecular Studies, Polish Academy of Sciences, Lodz, Poland
Kelnar I.; Institute of Macromolecular Chemistry, Academy of Sciences of the Czech Republic, Prague, Czech Republic (literal)
- Titolo
- Quaternized Xylan and sulfate films (literal)
- Abstract
- Xylan quaternized sulfate films were prepared from beech xylan (X) and compared with fully sulfated xylan films (XS). When quaternized xylan (QX) was prepared in the first step (DSQ = 0.55), than by sulfation of QX in the second step the fully substituted ampholytic derivative (QXS; DSQ = 0.33; DSS = 1.67) could be obtained. By sulfation in first step, xylan sulphate (SX, DSS = 0.70) was obtained and by subsequent quaternization, SXQ film with DSQ = 0.55 and DSS = 0.33 which contained partially unsubstituted hydroxyls. The molar masses (Mn) of the film's soluble parts were increasing in order X < SX < SXQ < QX < XS < QXS. In all films there were some insoluble particles present as determined by the amount of recovered masses by SEC-MALS. The materials were further characterized by AFM, XRD, TG/DTG/DTA, NMR and mechanical testing. QXS and SXQ could form mechanically more stable films than XS specimens (literal)