Structural and luminescence properties of Eu and Er implanted Bi2O3 nanowires for optoelectronic applications (Articolo in rivista)

Type
Label
  • Structural and luminescence properties of Eu and Er implanted Bi2O3 nanowires for optoelectronic applications (Articolo in rivista) (literal)
Anno
  • 2013-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1039/c3tc31989j (literal)
Alternative label
  • Vila, Maria; Diaz-Guerra, Carlos; Lorenz, Katharina; Piqueras, Javier; Alves, Eduardo; Nappini, Silvia; Magnano, Elena (2013)
    Structural and luminescence properties of Eu and Er implanted Bi2O3 nanowires for optoelectronic applications
    in JOURNAL OF MATERIALS CHEMISTRY C
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Vila, Maria; Diaz-Guerra, Carlos; Lorenz, Katharina; Piqueras, Javier; Alves, Eduardo; Nappini, Silvia; Magnano, Elena (literal)
Pagina inizio
  • 7920 (literal)
Pagina fine
  • 7929 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 1 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
  • 10 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 47 (literal)
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • Complutense University of Madrid; Instituto Superior Tecnico; IOM CNR (literal)
Titolo
  • Structural and luminescence properties of Eu and Er implanted Bi2O3 nanowires for optoelectronic applications (literal)
Abstract
  • Effective Er and Eu doping of alpha-Bi2O3 nanowires has been achieved by ion implantation. The nanostructures exhibit stable and efficient photoluminescence emission at room temperature after adequate annealing. X-ray photoelectron and X-ray absorption spectroscopy measurements reveal the incorporation of Er and Eu ions only in the desired trivalent charge state. The structural recovery of the implantation damage after thermal treatments was monitored by micro-Raman spectroscopy. Nanowires implanted with 300 keV ions and fluences in the range of 2 x 10(15) to 8 x 10(15) cm(-2) show luminescence emission after annealing at 450 degrees C and 550 degrees C. Samples implanted with Eu ions show Eu3+ emission lines at 543 nm (D-5(1)-F-7(1) transition), 587 nm (D-5(1)-F-7(3) transition), 613 and 622 nm (D-5(0)-F-7(2) transitions). Er-implanted nanowires show luminescence in the red range between 650 and 680 nm, corresponding to Er3+ F-2(9/2)-I-4(15/2) transitions. High angle annular dark field scanning transmission electron microscopy observations combined with energy dispersive X-ray microanalysis measurements reveal the formation of dopant-rich regions at higher fluences, leading to a reduced optical signal. (literal)