Chemical treatments for improving adhesion between electrospun nanofibers and fabrics (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Chemical treatments for improving adhesion between electrospun nanofibers and fabrics (Articolo in rivista) (literal)

Anno

• 2014-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1002/app.39766 (literal)

Alternative label

• Varesano A.; Rombaldoni F.; Tonetti C.; Di Mauro S.; Mazzuchetti G. (2014)
  Chemical treatments for improving adhesion between electrospun nanofibers and fabrics
  in Journal of applied polymer science (Online)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Varesano A.; Rombaldoni F.; Tonetti C.; Di Mauro S.; Mazzuchetti G. (literal)

Pagina inizio

• 39766 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://www.scopus.com/inward/record.url?eid=2-s2.0-84886591577&partnerID=q2rCbXpz (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 131 (literal)

Rivista

• Journal of applied polymer science (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 2 (literal)

Note

• Scopu (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Varesano A.; Rombaldoni F.; Tonetti C.; Mazzuchetti G. CNR-ISMAC-Biella; Di Mauro S. Politecnico di Torino (literal)

Titolo

• Chemical treatments for improving adhesion between electrospun nanofibers and fabrics (literal)

Abstract

• Nanofiber-coated fabrics have potential uses in filters and protective clothing. One major challenge is to ensure good adhesion of nanofibers to the fabrics achieving satisfactory durability against abrasion for practical use. This work is aimed to study adhesion mechanisms and their improvement between nanofibers and textile substrates; to achieve this goal cotton fabrics were treated with an alkali solution, while nylon fabrics were treated with ethanol. Adhesion of polyamide-6 electrospun nanofiber layer to fabrics was evaluated by means of a peeling test. Treated fabrics showed improved bonding towards nanofibers: adhesion energy was ~0.58 J m-2 for both untreated fabrics, and after treatments increased to 0.93 and 0.86 J m-2 for cotton and nylon ones, respectively. Optical observations revealed that nanofibers deposited on fabrics are mainly linked to external protruding fibers (i.e., fabric hairiness). Therefore, surface hairiness seems to be the critical factor limiting adhesion. (literal)

Prodotto di

• Materiali tessili, Tecnofibre e Processi industriali per la filiera tessile (SP.P01.031.001) (Modulo)
• Istituto per lo studio delle macromolecole (ISMAC) (Istituto)

Autore CNR

• ALESSIO VARESANO (Persona)
• CINZIA TONETTI (Unità di personale esterno)
• FABIO ROMBALDONI (Unità di personale esterno)
• GIORGIO MAZZUCHETTI (Unità di personale interno)

Insieme di parole chiave

• Parole chiave di "Chemical treatments for improving adhesion between electrospun nanofibers and fabrics" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• ALESSIO VARESANO (Persona)
• GIORGIO MAZZUCHETTI (Unità di personale interno)
• CINZIA TONETTI (Unità di personale esterno)
• FABIO ROMBALDONI (Unità di personale esterno)

Prodotto

• Istituto per lo studio delle macromolecole (ISMAC) (Istituto)
• Materiali tessili, Tecnofibre e Processi industriali per la filiera tessile (SP.P01.031.001) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of applied polymer science (Rivista)

Insieme di parole chiave di

• Parole chiave di "Chemical treatments for improving adhesion between electrospun nanofibers and fabrics" (Insieme di parole chiave)