Influence of Packing on Low Energy Vibrations of Densified Glasses (Articolo in rivista)

Type
Label
  • Influence of Packing on Low Energy Vibrations of Densified Glasses (Articolo in rivista) (literal)
Anno
  • 2013-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1103/PhysRevLett.111.245502 (literal)
Alternative label
  • Carini, Giovanni, Jr.; Carini, Giuseppe; D'Angelo, Giovanna; Tripodo, Gaspare; Di Marco, Gaetano; Vasi, Cirino; Gilioli, Edmondo (2013)
    Influence of Packing on Low Energy Vibrations of Densified Glasses
    in Physical review letters (Print); The American Physical Society, College Park, MD 20740-3844 (Stati Uniti d'America)
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Carini, Giovanni, Jr.; Carini, Giuseppe; D'Angelo, Giovanna; Tripodo, Gaspare; Di Marco, Gaetano; Vasi, Cirino; Gilioli, Edmondo (literal)
Pagina inizio
  • 245502-1 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url
  • http://journals.aps.org/prl/abstract/10.1103/PhysRevLett.111.245502 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 111 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
  • 5 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 24 (literal)
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • 1 IPCF del C.N.R., Sede di Messina, I-98158 Messina, Italy; 2 Dipartimento di Fisica e di Scienze della Terra, Università degli Studi di Messina, I-98166 Messina, Italy; 3 IMEM del C.N.R., Area delle Scienze, I-43010 Parma, Italy (literal)
Titolo
  • Influence of Packing on Low Energy Vibrations of Densified Glasses (literal)
Abstract
  • A comparative study of Raman scattering and low temperature specific heat capacity has been performed on samples of B2O3, which have been high-pressure quenched to go through different glassy phases having growing density to the crystalline state. It has revealed that the excess volume characterizing the glassy networks favors the formation of specific glassy structural units, the boroxol rings, which produce the boson peak, a broad band of low energy vibrational states. The decrease of boroxol rings with increasing pressure of synthesis is associated with the progressive depression of the excess low energy vibrations until their full disappearance in the crystalline phase, where the rings are missing. These observations prove that the additional soft vibrations in glasses arise from specific units whose formation is made possible by the poor atomic packing of the network. (literal)
Editore
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Prodotto
Autore CNR di
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Editore di
Insieme di parole chiave di
data.CNR.it