InZnO nanorods obtained via zinc vapour phase deposition on liquid indium seeded substrates (Articolo in rivista)

Type
Label
  • InZnO nanorods obtained via zinc vapour phase deposition on liquid indium seeded substrates (Articolo in rivista) (literal)
Anno
  • 2014-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1039/c3ce42095g (literal)
Alternative label
  • Calestani, Davide; Dhanabalan, Sathish Chander; Villani, Marco; Lazzarini, Laura; Zappettini, Andrea (2014)
    InZnO nanorods obtained via zinc vapour phase deposition on liquid indium seeded substrates
    in CrystEngComm (Camb., Online); ROYAL SOC CHEMISTRY, THOMAS GRAHAM HOUSE,, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND (Regno Unito)
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Calestani, Davide; Dhanabalan, Sathish Chander; Villani, Marco; Lazzarini, Laura; Zappettini, Andrea (literal)
Pagina inizio
  • 1696 (literal)
Pagina fine
  • 1701 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url
  • http://pubs.rsc.org/en/Content/ArticleLanding/2014/CE/c3ce42095g#!divAbstract (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 16 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
  • 6 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 9 (literal)
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • IMEM CNR, Parco Area Sci 37-A, I-43124 Parma, Italy (literal)
Titolo
  • InZnO nanorods obtained via zinc vapour phase deposition on liquid indium seeded substrates (literal)
Abstract
  • Indium zinc oxide nanorods (IZO-NRs) have been obtained at temperatures lower than 500 degrees C in a conventional CVD system, with a resulting indium concentration larger than 1%. The growth of these ternary oxide nanostructures has been obtained, simply starting from the corresponding metals, thanks to the direct deposition on the growth substrate of an In layer, which in its molten state and upon mixture with Zn acts as a growth seed. The obtained In concentration corresponds to the value required to achieve metallic behaviour and makes this ternary oxide an ideal TCO (transparent conducting oxide), while the used temperature range (<500 degrees C) makes this vapour phase process compatible also with commercial glass substrates, without using any expensive metal-organic precursor. (literal)
Editore
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Autore CNR di
Prodotto
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Editore di
Insieme di parole chiave di
data.CNR.it