Raman spectroscopy study of the interface structure in (CaCuO2)n/(SrTiO3)m superlattices (Articolo in rivista)
- Type
- Label
- Raman spectroscopy study of the interface structure in (CaCuO2)n/(SrTiO3)m superlattices (Articolo in rivista) (literal)
- Anno
- 2013-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1063/1.4828358 (literal)
- Alternative label
D. Di Castro1, S. Caramazza2, D. Innocenti1, G. Balestrino1, C. Marini3, P. Dore4 and P. Postorino5 (2013)
Raman spectroscopy study of the interface structure in (CaCuO2)n/(SrTiO3)m superlattices
in Applied physics letters
(literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- D. Di Castro1, S. Caramazza2, D. Innocenti1, G. Balestrino1, C. Marini3, P. Dore4 and P. Postorino5 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
- Note
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- 1 CNR-SPIN and Dipartimento di Ingegneria Civile e Ingegneria Informatica, Università di Roma Tor Vergata, Via del Politecnico 1, 00133 Roma, Italy
2 Dipartimento di Fisica, Università di Roma Sapienza, Piazzale Aldo Moro 2, 00185 Roma, Italy
3 European Synchrotron Radiation Facility, BP 220, 38043 Grenoble Cedex, France
4 CNR-SPIN and Dipartimento di Fisica, Università di Roma Sapienza, Piazzale Aldo Moro 2, 00185 Roma, Italy
5 CNR-IOM and Dipartimento di Fisica, Università di Roma Sapienza, Piazzale Aldo Moro 2, 00185 Roma, Italy (literal)
- Titolo
- Raman spectroscopy study of the interface structure in (CaCuO2)n/(SrTiO3)m superlattices (literal)
- Abstract
- Raman spectra of CaCuO2/SrTiO3 superlattices show clear spectroscopic marker of two structures formed in CaCuO2 at the interface with SrTiO3. For non-superconducting superlattices, grown in low oxidizing atmosphere, the 425 cm(-1) frequency of oxygen vibration in CuO2 planes is the same as for CCO films with infinite layer structure (planar Cu-O coordination). For superconducting superlattices grown in highly oxidizing atmosphere, a 60 cm(-1) frequency shift to lower energy occurs. This is ascribed to a change from planar to pyramidal Cu-O coordination because of oxygen incorporation at the interface. Raman spectroscopy proves to be a powerful tool for interface structure investigation. (c) 2013 AIP Publishing LLC. (literal)