Fabrication of superconducting Nd2-xCexCuO4 +/-delta films by automated dc sputtering technique (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Fabrication of superconducting Nd2-xCexCuO4 +/-delta films by automated dc sputtering technique (Articolo in rivista) (literal)

Anno

• 2013-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.physc.2013.09.010 (literal)

Alternative label

• A. Guarino a, b, G. Patimo a, A. Vecchione b, T. Di Luccio c, A. Nigro a, b (2013)
  Fabrication of superconducting Nd2-xCexCuO4 +/-delta films by automated dc sputtering technique
  in Physica. C, Superconductivity (Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• A. Guarino a, b, G. Patimo a, A. Vecchione b, T. Di Luccio c, A. Nigro a, b (literal)

Pagina inizio

• 146 (literal)

Pagina fine

• 152 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 495 (literal)

Rivista

• Physica. C, Superconductivity (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• a Dipartimento di Fisica \"E. R. Caianiello\", via Giovanni Paolo II 132, I-84084 Fisciano (SA), Italy b CNR-SPIN, via Giovanni Paolo II 132, I-84084 Fisciano (SA), Italy c ENEA Centro Ricerche Portici, UTTP NANO, Piazzale E. Fermi 1, I-80055 Portici (NA), Italy (literal)

Titolo

• Fabrication of superconducting Nd2-xCexCuO4 +/-delta films by automated dc sputtering technique (literal)

Abstract

• Superconducting electron-doped Nd2-xCexCuO4±? films have been successfully prepared on (0 0 1) SrTiO3 substrates by an automated dc sputtering system. The composition of the samples has been measured by wavelength dispersive spectroscopy, and the crystalline structure has been investigated by high resolution X-ray diffraction technique. Measurements by backscattered electrons has been also used in order to deeply analyze the microstructure of the samples. We have found that the quality of the films is highly sensitive to the deposition conditions and that the superconductivity is reached only after suitable heat treatments at temperature above to 850 °C in an oxygen-reducing atmosphere. The films deposited with the optimized conditions show a high degree of epitaxial growth, moreover an increase of c lattice parameter is found in all the superconducting samples. X-ray reflectivity measurements on thin films by using synchrotron radiation proved that smooth surfaces (roughness less than 2 nm) and neat interfaces characterize the films through the whole thickness. (literal)

Prodotto di

• Realizzazione e studio di materiali con forti correlazioni di spin, carica ed orbitale (MD.P04.025.001) (Modulo)
• Proprietà statiche e dinamiche in superconduttori del II tipo, e loro funzionalità nelle applicazioni per l'energia (MD.P04.023.002) (Modulo)

Autore CNR

• ANITA GUARINO (Unità di personale esterno)
• ANTONIO VECCHIONE (Persona)
• ANGELA NIGRO (Unità di personale esterno)

Insieme di parole chiave

• Keywords of "Fabrication of superconducting Nd2-xCexCuO4 +/-delta films by automated dc sputtering technique" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• ANITA GUARINO (Unità di personale esterno)
• ANGELA NIGRO (Unità di personale esterno)
• ANTONIO VECCHIONE (Persona)

Prodotto

• Proprietà statiche e dinamiche in superconduttori del II tipo, e loro funzionalità nelle applicazioni per l'energia (MD.P04.023.002) (Modulo)
• Realizzazione e studio di materiali con forti correlazioni di spin, carica ed orbitale (MD.P04.025.001) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Physica. C, Superconductivity (Rivista)

Insieme di parole chiave di

• Keywords of "Fabrication of superconducting Nd2-xCexCuO4 +/-delta films by automated dc sputtering technique" (Insieme di parole chiave)