Transparent conducting oxides for high temperature processing (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Transparent conducting oxides for high temperature processing (Articolo in rivista) (literal)

Anno

• 2014-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.egypro.2013.12.005 (literal)

Alternative label

• M. Allegrezza, M. Canino, M. Bellettato, C. Summonte (2014)
  Transparent conducting oxides for high temperature processing
  in Energy procedia (Online); Elsevier, Amsterdam (Paesi Bassi)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• M. Allegrezza, M. Canino, M. Bellettato, C. Summonte (literal)

Pagina inizio

• 23 (literal)

Pagina fine

• 31 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://www.sciencedirect.com/science/article/pii/S1876610213018183 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 44 (literal)

Rivista

• Energy procedia (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 9 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• CNR-IMM (literal)

Titolo

• Transparent conducting oxides for high temperature processing (literal)

Abstract

• Abstract Indium tin oxide (ITO) thin films were deposited by magnetron sputtering from a ceramic target, and annealed at temperatures up to 1000°C in N2 atmosphere. Some samples were capped in a-Si:H or spin-on glass to prevent residual oxygen contamination from the annealing ambient, and annihilation of oxygen vacancies. The electrical and optical properties were measured before and after annealing. It is found that the protecting layer effectively limits the ITO degradation up to 900°C, whereas high transparency is preserved in all cases. The results indicate the applicability of the procedure to high temperature devices, and opens the way to the application of a variety of nanostructured materials in advanced photovoltaic devices. (literal)

Editore

• Elsevier (Editore)

Prodotto di

• Institute for microelectronics and microsystems (IMM) (Istituto)

Autore CNR

• CATERINA SUMMONTE (Persona)
• MARIACONCETTA CANINO (Unità di personale interno)
• MARCO ALLEGREZZA (Persona)
• michele bellettato (Unità di personale esterno)

Incoming links:

Prodotto

• Institute for microelectronics and microsystems (IMM) (Istituto)
• http://www.cnr.it/ontology/cnr/individuo/modulo/ID6827

Autore CNR di

• CATERINA SUMMONTE (Persona)
• michele bellettato (Unità di personale esterno)
• MARCO ALLEGREZZA (Persona)
• MARIACONCETTA CANINO (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Energy procedia (Rivista)

Editore di

• Elsevier (Editore)