Reduction of Nitrate Ions at Rh-Modified Ni Foam Electrodes (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Reduction of Nitrate Ions at Rh-Modified Ni Foam Electrodes (Articolo in rivista) (literal)

Anno

• 2013-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1007/s12678-013-0129-2 (literal)

Alternative label

• Verlato E.; Cattarin S.; Comisso N.; Mattarozzi L.; Musiani M.; Vázquez-Gómez L.; (2013)
  Reduction of Nitrate Ions at Rh-Modified Ni Foam Electrodes
  in Electrocatalysis (N. Y., Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Verlato E.; Cattarin S.; Comisso N.; Mattarozzi L.; Musiani M.; Vázquez-Gómez L.; (literal)

Pagina inizio

• 203 (literal)

Pagina fine

• 211 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://link.springer.com/article/10.1007%2Fs12678-013-0129-2 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 4 (literal)

Rivista

• Electrocatalysis (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 9 (literal)

Note

• ISI Web of Science (WOS) (literal)
• Scopu (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• 1-6 : IENI CNR, Corso Stati Uniti 4, 35127 Padua, Italy (literal)

Titolo

• Reduction of Nitrate Ions at Rh-Modified Ni Foam Electrodes (literal)

Abstract

• Commercial Ni foams were modified by spontaneous deposition of Rh nanoparticles, achieved by immersion of foam samples in acid, deaerated Na3RhCl6 solutions, at open circuit. The surface area of the Rh deposits was estimated, for different Rh loadings, by measuring the H adsorption/desorption charge. The surface area per unit Rh mass was found to exceed 50 m2 g-1, for loading values below 2 mg cm-3. The Rh-modified Ni foam electrodes were used as cathodes for the reduction of nitrate ions, and showed good catalytic activity, increasing with the Rh loading in a sublinear way; thus, the mass activity of the electrodes was higher at low loading. Prolonged electrolyses showed that the Rh-modified Ni foam electrodes underwent only moderate poisoning. Ion chromatography was used to assess the reaction products: irrespective of the Rh loading, ammonia was the main product, and nitrite accounted only for a few percent of the reduced nitrate. The beneficial effect of forcing a solution flow through the foam pores on the nitrate reduction current was shown. (literal)

Prodotto di

• Materiali e Processi per l'Elettrochimica dell'Idrogeno e l'Elettrocatalisi (ET.P06.011.001) (Modulo)
• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)

Autore CNR

• ENRICO VERLATO (Unità di personale interno)
• NICOLA COMISSO (Unità di personale interno)
• LOURDES VAZQUEZ GOMEZ (Persona)
• LUCA MATTAROZZI (Unità di personale esterno)
• MARCO MUSIANI (Persona)
• SANDRO CATTARIN (Unità di personale interno)

Incoming links:

Autore CNR di

• NICOLA COMISSO (Unità di personale interno)
• MARCO MUSIANI (Persona)
• SANDRO CATTARIN (Unità di personale interno)
• LUCA MATTAROZZI (Unità di personale esterno)
• LOURDES VAZQUEZ GOMEZ (Persona)
• ENRICO VERLATO (Unità di personale interno)

Prodotto

• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)
• Materiali e Processi per l'Elettrochimica dell'Idrogeno e l'Elettrocatalisi (ET.P06.011.001) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Electrocatalysis (Rivista)