Degree of conversion and interfacial nanoleakage expression of three one-step self-etch adhesives. (Articolo in rivista)

Type

Label

Degree of conversion and interfacial nanoleakage expression of three one-step self-etch adhesives. (Articolo in rivista) (literal)

Anno

Alternative label

Navarra CO, Cadenaro M, Codan B, Mazzoni A, Sergo V, De Stefano Dorigo E, Breschi L. (2009)
Degree of conversion and interfacial nanoleakage expression of three one-step self-etch adhesives.
in European journal of oral sciences
(literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

Navarra CO, Cadenaro M, Codan B, Mazzoni A, Sergo V, De Stefano Dorigo E, Breschi L. (literal)

Pagina inizio

Pagina fine

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

Rivista

Note

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

Department of SAU & FAL, University of Bologna, Bologna, Italy; Division of Dental Sciences and Biomaterials, Department of Biomedicine, University of Trieste, Trieste, Italy; Department of Fixed Prosthodontics and Dental Materials, University of Siena, Siena, Italy; IGM-CNR, Unit of Bologna, c/o IOR, Bologna, Italy (literal)

Titolo

Degree of conversion and interfacial nanoleakage expression of three one-step self-etch adhesives. (literal)

Abstract

Suboptimally polymerized monomers may be responsible for the reduced material properties of simplified adhesives and their inherent bonded interface instability. This study was performed to determine the degree of cure within the hybrid layers produced by three one-step self-etch adhesives in situ using Raman microspectroscopy and to investigate nanoleakage expression. Dentin disks were bonded with AdheSE One, Adper Prompt L-Pop, or iBond. Composite layers of 2-mm thickness were built up in bulk on the polymerized adhesive surfaces and then the adhesive-dentin interfaces were exposed to a micro-Raman beam. Adhesive penetration was calculated using the relative intensities of bands associated with mineral and adhesive, and the degree of conversion (DC) was evaluated. Interfacial nanoleakage expression was evaluated on the same specimens. The DC values for the tested adhesives were found to increase in the following order: AdheSE One (48 +/- 16%) < Adper Prompt L-Pop (83 +/- 2%) = iBond (90 +/- 6%; P < 0.05). AdheSE One showed greater nanoleakage expression than iBond or Adper Prompt L-Pop. Increased nanoleakage expression was associated with AdheSE One that showed the lowest DC. This suggests that a low DC may affect the quality and the long-term stability of the adhesive interface owing to the elution of unreacted monomers forming a porous and highly permeable hybrid layer. (literal)