Mössbauer spectroscopy of 57Fe in alpha-Al2O3 following implantation of 57Mn* (Articolo in rivista)

Type

Label

Mössbauer spectroscopy of 57Fe in alpha-Al2O3 following implantation of 57Mn* (Articolo in rivista) (literal)

Anno

Alternative label

H. P. Gunnlaugsson1, R. Mantovan2, T. E. Mølholt3, D. Naidoo4, K. Johnston5, H. Masenda4, K. Bharuth-Ram6, G. Langouche7, S. Ólafsson3, R. Sielemann8, G. Weyer1, Y. Kobayashi9, the ISOLDE collaboration5 (2010)
Mössbauer spectroscopy of 57Fe in alpha-Al2O3 following implantation of 57Mn*
in Hyperfine interactions (Dordr., Online); Kluwer, Dordrecht (Paesi Bassi)
(literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

H. P. Gunnlaugsson1, R. Mantovan2, T. E. Mølholt3, D. Naidoo4, K. Johnston5, H. Masenda4, K. Bharuth-Ram6, G. Langouche7, S. Ólafsson3, R. Sielemann8, G. Weyer1, Y. Kobayashi9, the ISOLDE collaboration5 (literal)

Pagina inizio

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

Rivista

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

1. Department of Physics and Astronomy, Aarhus University, 8000, Århus C, Denmark 2. Laboratorio MDM, IMM-CNR, Via Olivetti 2, 20041, Agrate Brianza, (MB), Italy 3. Science Institute, University of Iceland, Dunhaga 3, 107, Reykjavík, Iceland 4. School of Physics, University of the Witwatersrand, Private Bag 3, WITS, 2050, South Africa 5. PH Dept, ISOLDE/CERN, 1211, Geneva 23, Switzerland 6. School of Physics, University of KwaZulu-Natal, Durban, 4001, South Africa 7. Instituut voor Kern- en Stralingsfysica, University of Leuven, 3001, Leuven, Belgium 8. Helmholtz-Zentrum Berlin für Materialien und Energie, 14109, Berlin, Germany 9. The Institute of Physical and Chemical Research (RIKEN), Wako, Saitama, 351-0198, Japan (literal)

Titolo

Mössbauer spectroscopy of 57Fe in alpha-Al2O3 following implantation of 57Mn* (literal)

Abstract

The valence state and annealing reactions of Mn/Fe in single crystalline ?-Al2O3 have been determined following low fluence (<1012 cm - 2) 60 keV implantations of 57Mn + (T1/2 = 1.5 min) and emission Mössbauer spectroscopy on the 57m Fe daughter nuclei in the temperature range from 110-700 K. At 110 K, most probe atoms are found in the Fe2 + state in amorphous surroundings due to the implantation damage. A fraction of the Fe is found in cubic environment, possibly nano-precipitates of ?-Al2O3. This site is found to disappear from the spectra above 500 K. Annealing of the damage sites at increasing temperatures leads first to increased incorporation of the probe atoms as Fe3 + on Al sites, and, above room temperature, also as Fe4 + . The Fe3 + sub-spectrum is masked by slow paramagnetic relaxations following a T2 dependence, as expected for a two-phonon Raman process. Our data is consistent with data from 57Co and 57Fe implantations, suggesting a general increase in the average Fe valence state with lower implantation dose and negligible annealing reactions at room temperature. (literal)