Growth and morphology of Te films on Mo (Articolo in rivista)

Type
Label
  • Growth and morphology of Te films on Mo (Articolo in rivista) (literal)
Anno
  • 1999-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1016/S0040-6090(99)00383-1 (literal)
Alternative label
  • Sergio Valeri, Paola Paradisi, Paola Luches, Alessandro di Bona (1999)
    Growth and morphology of Te films on Mo
    in Thin solid films (Print); Elsevier BV, Amsterdam (Paesi Bassi)
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Sergio Valeri, Paola Paradisi, Paola Luches, Alessandro di Bona (literal)
Pagina inizio
  • 114 (literal)
Pagina fine
  • 118 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url
  • http://www.sciencedirect.com/science/article/pii/S0040609099003831 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 352 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
  • 5 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 1-2 (literal)
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • Istituto Nazionale per la Fisica della Materia and Dipartimento di Fisica, Università di Modena e Reggio Emilia, via Campi 213/a, 41100 Modena, Italy (literal)
Titolo
  • Growth and morphology of Te films on Mo (literal)
Abstract
  • Tellurium films were deposited by thermal evaporation on a molybdenum substrate held at 120°C. The growth of the films was monitored by quantitative X-ray photoelectron spectroscopy and by atomic force microscopy. Reaction of the Te films with K vapour was also used to evaluate the thickness of the films. It has been found that for low exposures Te grows as a uniform layer, up to a thickness of about 0.4 nm. For higher exposures we observed the formation of islands of increasing thickness that cover an increasing fraction of the substrate, the remaining fraction being covered by a continuous thin layer. Implications of such a morphology on the performances of Te-based photocathodes in photo-injectors technology are discussed. (literal)
Editore
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Autore CNR di
Prodotto
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Editore di
Insieme di parole chiave di
data.CNR.it