Experimental features affecting the transparency of YAG ceramics (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Experimental features affecting the transparency of YAG ceramics (Articolo in rivista) (literal)

Anno

• 2011-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.optmat.2010.09.016 (literal)

Alternative label

• Laura Esposito, Andreana Piancastelli, Anna Luisa Costa, Marina Serantoni, Guido Toci, Matteo Vannini, (2011)
  Experimental features affecting the transparency of YAG ceramics
  in Optical materials
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Laura Esposito, Andreana Piancastelli, Anna Luisa Costa, Marina Serantoni, Guido Toci, Matteo Vannini, (literal)

Pagina inizio

• 713 (literal)

Pagina fine

• 721 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 33 (literal)

Rivista

• Optical materials (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 9 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 5 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• CNR ISTEC, CNR IFAC (literal)

Titolo

• Experimental features affecting the transparency of YAG ceramics (literal)

Abstract

• This article focuses on the importance of the ceramic production process for the final transparency and overall optical quality of materials to be used as laser hosts. YAG-based ceramics are prepared starting from commercial powders. The materials are prepared by reactive sintering in a clean atmosphere and under high vacuum. Nd or Yb are selected as active elements as the more appropriate for high energy and high peak power lasers. The powder type and treatment and the solvent removal technique are described in detail as well as the experimental conditions adopted during shaping. The influence of the pre-sintering and sintering cycles on the reaction among the involved oxides and on the microstructure after sintering is shown. The optical characterization is also reported. (literal)

Prodotto di

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Dispositivi e materiali laser innovativi e metodi spettroscopici avanzati (MD.P03.002.001) (Modulo)
• Institute of applied physics \"Nello Carrara\" (IFAC) (Istituto)
• Materiali ceramici trasparenti per applicazioni ottiche ed elettromagnetiche (SP.P01.033.003) (Modulo)

Autore CNR

• MATTEO VANNINI (Persona)
• GUIDO TOCI (Unità di personale interno)
• ANDREANA PIANCASTELLI (Unità di personale interno)
• ANNA LUISA COSTA (Persona)
• LAURA ESPOSITO (Unità di personale interno)

Incoming links:

Prodotto

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Institute of applied physics \"Nello Carrara\" (IFAC) (Istituto)
• Materiali ceramici trasparenti per applicazioni ottiche ed elettromagnetiche (SP.P01.033.003) (Modulo)
• Dispositivi e materiali laser innovativi e metodi spettroscopici avanzati (MD.P03.002.001) (Modulo)

Autore CNR di

• LAURA ESPOSITO (Unità di personale interno)
• MATTEO VANNINI (Persona)
• ANDREANA PIANCASTELLI (Unità di personale interno)
• GUIDO TOCI (Unità di personale interno)
• ANNA LUISA COSTA (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Optical materials (Rivista)