Micro injection moulding process and product characterization (Contributo in atti di convegno)

Type
Label
  • Micro injection moulding process and product characterization (Contributo in atti di convegno) (literal)
Anno
  • 2011-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1115/DETC2011-48301 (literal)
Alternative label
  • R.Surace, G. Trotta, A. Bongiorno, V. Bellantone, C. Pagano, and I. Fassi. (2011)
    Micro injection moulding process and product characterization
    in ASME 2011 International Design Engineering Technical Conferences and Computers and Information in Engineering Conference, IDETC/CIE 2011, Washington, DC; United States;, 28-31 agosto 2011
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • R.Surace, G. Trotta, A. Bongiorno, V. Bellantone, C. Pagano, and I. Fassi. (literal)
Pagina inizio
  • 433 (literal)
Pagina fine
  • 439 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#titoloVolume
  • Proceedings of the ASME Design Engineering Technical Conference (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 7 (literal)
Note
  • Google Scholar (literal)
  • Scopu (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • CNR ITIA (literal)
Titolo
  • Micro injection moulding process and product characterization (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#isbn
  • 9780791854846 (literal)
Abstract
  • Due to its high efficiency for the large scale production of polymeric parts, micro injection moulding is one of the key technologies of the new millennium. Although a lot of researches have been conducted to identify the most effective processing conditions for micro injection moulding, the comprehension of the influence of all parameters on the quality, the properties and the reliability of the moulded parts is still an issue. In this context, this study aims to evaluate the effects of the micro injection moulding process conditions on the tensile properties of micro parts, investigating the influence of three main process parameters: the injection speed, the mould temperature and the melt temperature. A full factorial plan has been applied to study the contributions of these parameters and a second study has been performed to understand the synergic interaction between the two temperatures on the tensile strength. Due to its high level of potential crystallinity, a typical semi-crystalline thermoplastic resin was used in the experiments. The results of the analysis showed a great influence of the mould temperature (T mould) on the ultimate tensile strength and of the melt temperature (T melt) on the deformation at the point of breaking; whereas the injection speed was significant on the overall mechanical performance. A new studied factor (T melt-T mould) could affect the resulting molecular structure and consequently the mechanical behaviour, but itself is not sufficient to thoroughly explain the observed behaviour. Moreover, the visual inspection of the deformation mechanism at break shows three distinctive trends demonstrating the great variability of the mechanical properties of micro-injected specimens due to process conditions. (literal)