Fabrication by rf-sputtering and diagnostics of Er3+/Yb3+ - activated silicahafnia waveguides (Comunicazione a convegno)
- Type
- Label
- Fabrication by rf-sputtering and diagnostics of Er3+/Yb3+ - activated silicahafnia waveguides (Comunicazione a convegno) (literal)
- Anno
- 2007-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1109/CLEOE-IQEC.2007.4386228 (literal)
- Alternative label
C.Armellini, A. Chiappini, A. Chiasera, M. Ferrari, V. Foglietti, Y. Jestin, A. Minotti, M. Montagna, E. Moser, G. Nunzi Conti, S. Pelli, G.C. Righini, C. Tosello (2007)
Fabrication by rf-sputtering and diagnostics of Er3+/Yb3+ - activated silicahafnia waveguides
in Conference Digest CLEO-Europe IQEC 2007 - 18th International Congress on Photonics in Europe, Munich, Germany, 17-22 June, 2007
(literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- C.Armellini, A. Chiappini, A. Chiasera, M. Ferrari, V. Foglietti, Y. Jestin, A. Minotti, M. Montagna, E. Moser, G. Nunzi Conti, S. Pelli, G.C. Righini, C. Tosello (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
- Note
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- CNR-IFN, Inst. Photonics and Nanotechnology, CSMFO Group, via Sommarive 14, 38050 Povo-Trento, Italy; Physics Dept., Trento University, CSMFO Group, via Sommarive 14, 38050 Povo-Trento, Italy; CNR-IFN, Inst. Photonics and Nanotechnohgy, MEMS Group, Via Cineto Romano 42, 00156 Roma, Italy; Centro Fermi, Compendio del Viminale, 00184 Roma, Italy; CNR-IFAC, N. Carrara Inst. Appl. Physics, via Madonna del Piano 10, 50019 Sesto Fiorentino-Firenze, Italy; CNR, Materials and Devices Dept., via dei Taurini 19, 00185 Roma, Italy (literal)
- Titolo
- Fabrication by rf-sputtering and diagnostics of Er3+/Yb3+ - activated silicahafnia waveguides (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#isbn
- Abstract
- SiO2-HfO2: Er3+-Yb3+ waveguide was prepared by multi-target rf-sputtering technique on silica substrate. The optical parameters were measured by an m-line apparatus operating at 543.5, 632.8, 1319 and 1542 nm. The structural properties were investigated with energy dispersive spectroscopy and Raman spectroscopy. The planar waveguide had a single-mode at 1.3 and 1.5 mum and an attenuation coefficient of 0.2 dB/cm at 1.5 mum was obtained. The 4I13/2 rarr 4I15/2 emission of Er3+ ion transition with a 42 nm bandwidth and a lifetime of 4.6 ms was observed upon excitation in the TE0 mode at 980 and 514.5 nm. Photoluminescence (PL) excitation spectroscopy was used to obtain information about the effective excitation efficiency of Er3+ ions by co-doping with Yb3+ ions and the spectrum reported indicates that an effectual energy transfer from ytterbium to erbium ions is present. Additional work is currently under way to investigate the effect of the Er3+/Yb3+ concentration and excitation power on the Er3+ fluorescence intensity at 1.53 mum. Rib waveguide was also produced by photolithography and wet etching process. PL measurements were performed using the TE0 mode excitation on the planar system, and injecting the laser light by a 20X microscope objective in the channel on the etched system. The spectral shape of the erbium emission at 1.5 mum obtained on the channel system is equal to that obtained on the planar system. The measurements of signal enhancement when pumping Erbium ions at 980 nm are in progress. (literal)
- Prodotto di
- Autore CNR
- Insieme di parole chiave
Incoming links:
- Prodotto
- Autore CNR di
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
- Insieme di parole chiave di