Fabrication and Characterization of Sol-Gel GeO2-SiO2 Erbium-Doped Planar Waveguides (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Fabrication and Characterization of Sol-Gel GeO2-SiO2 Erbium-Doped Planar Waveguides (Articolo in rivista) (literal)

Anno

• 1999-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1023/A:1008618621828 (literal)

Alternative label

• A. Martucci, G. Brusatin, M. Guglielmi, C. Strohhöfer, J. Fick, S. Pelli, G.C. Righini (1999)
  Fabrication and Characterization of Sol-Gel GeO2-SiO2 Erbium-Doped Planar Waveguides
  in Journal of sol-gel science and technology; Kluwer, Dordrecht (Paesi Bassi)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• A. Martucci, G. Brusatin, M. Guglielmi, C. Strohhöfer, J. Fick, S. Pelli, G.C. Righini (literal)

Pagina inizio

• 535 (literal)

Pagina fine

• 539 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://link.springer.com/article/10.1023%2FA%3A1008618621828 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 13 (literal)

Rivista

• Journal of sol-gel science and technology (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 5 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 1-3 (literal)

Note

• Scopu (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Dipto. Ingegneria Mecc. - Settore M., Università di Padova, Via Marzolo, 9, 35131 Padova, Italy Lab. d'Electromagnetisme M., ENSERG, BP 257, 38016 Grenoble, France I.R.O.E.-C.N.R., Via Panciatichi 64, 50125 Firenze, Italy (literal)

Titolo

• Fabrication and Characterization of Sol-Gel GeO2-SiO2 Erbium-Doped Planar Waveguides (literal)

Abstract

• GeO2-SiO2 sol-gel planar waveguides doped with Er were deposited by spinning on silica substrates. P2O5 or Al2O3 were used as co-dopants to improve erbium dissolution in the GeO2-SiO2 matrix. Multilayer amorphous films were obtained at 600 or 700°C. Er ions in the planar waveguide pumped at 980 nm showed fluorescence features around 1530 nm. Narrow fluorescence spectra (~20 nm) and long lifetimes (~6 ms) were found in P2O5 co-doped samples, whereas Al2O3 co-doping gave wider spectra (~50 nm) with slightly lower lifetimes (~5 ms). The quenching concentration in the Al2O3 co-doped samples was 0.9 mol% Er. Heat treatments in CCl4 improve the active properties and the addition of Yb enhances the pump absorption efficiency. (literal)

Editore

• Kluwer (Editore)

Prodotto di

• Institute of applied physics \"Nello Carrara\" (IFAC) (Istituto)
• Materiali e dispositivi attivi per le telecomunicazioni e la sensoristica (MD.P03.001.001) (Modulo)

Autore CNR

• STEFANO PELLI (Persona)
• GIANCARLO RIGHINI (Persona)

Insieme di parole chiave

• Keywords of "Fabrication and Characterization of Sol-Gel GeO2-SiO2 Erbium-Doped Planar Waveguides" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute of applied physics \"Nello Carrara\" (IFAC) (Istituto)
• Materiali e dispositivi attivi per le telecomunicazioni e la sensoristica (MD.P03.001.001) (Modulo)

Autore CNR di

• STEFANO PELLI (Persona)
• GIANCARLO RIGHINI (Persona)

Editore di

• Kluwer (Editore)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of sol-gel science and technology (Rivista)

Insieme di parole chiave di

• Keywords of "Fabrication and Characterization of Sol-Gel GeO2-SiO2 Erbium-Doped Planar Waveguides" (Insieme di parole chiave)