Conductivity studies of sol-gel prepared BaCe0.85-xZr xY0.15O3-´ solid electrolytes using impedance spectroscopy (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Conductivity studies of sol-gel prepared BaCe0.85-xZr xY0.15O3-´ solid electrolytes using impedance spectroscopy (Articolo in rivista) (literal)

Anno

• 2009-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1007/s10800-009-9932-0 (literal)

Alternative label

• L. Doubova; S. Barison; S. Boldrini; M. Fabrizio; C. Mortalò; C. Pagura (2009)
  Conductivity studies of sol-gel prepared BaCe0.85-xZr xY0.15O3-´ solid electrolytes using impedance spectroscopy
  in Journal of Applied Electrochemistry
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• L. Doubova; S. Barison; S. Boldrini; M. Fabrizio; C. Mortalò; C. Pagura (literal)

Pagina inizio

• 2129 (literal)

Pagina fine

• 2141 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://www.springerlink.com/content/bk8258w05u681060/ (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 39 (literal)

Rivista

• Journal of Applied Electrochemistry (Rivista)

Note

• Scopu (literal)
• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Istituto per l’Energetica e le Interfasi (IENI), Consiglio Nazionale delle Ricerche (CNR), Corso Stati Uniti 4, 35127 Padova, Italy (literal)

Titolo

• Conductivity studies of sol-gel prepared BaCe0.85-xZr xY0.15O3-´ solid electrolytes using impedance spectroscopy (literal)

Abstract

• A systematic investigation on doped barium cerate perovskites on conductivity was performed by means of ac electrochemical impedance spectroscopy technique. BaCe0.85-xZrxY0.15O3-d powders (x=0, 0.1, 0.2, 0.3, 0.4) were prepared by a modified sol-gel Pechini method and sintered at 1250°C -1450°C, depending of Zr content, to obtain good densities (93-97 % of the theoretical ones). The measured total conductivities for these solid solutions in three different atmospheres were reported: in dry oxygen, in dry nitrogen and wet (0.5 bar H2O) hydrogen (5%H2/Ar) atmospheres. Arrhenius plots recorded in dry oxygen as well as in dry nitrogen showed some residual hydration which remained in the specimens upon initial heating. The compositions with x=0.3 and 0.4 gave conductivities close to 10-2 S/cm in 5%H2/Ar /H2O atmosphere at 600°C. The isothermal conductivities values showed a little variation for x from 0.2 to 0.4 between 500 and 800°C. (literal)

Prodotto di

• Leghe metalliche e ossidi nanostrutturati per dispositivi IT-SOFC, per nanofluidi, per materiali termoelettrici e loro applicazioni industriali (ET.P06.009.001) (Modulo)
• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)

Autore CNR

• SIMONA BARISON (Persona)
• MONICA FABRIZIO (Unità di personale interno)
• STEFANO BOLDRINI (Persona)
• CESARE PAGURA (Persona)
• CECILIA MORTALO' (Unità di personale interno)
• LIOUDMILA DOUBOVA (Unità di personale interno)

Insieme di parole chiave

• Parole chiave di "Conductivity studies of sol-gel prepared BaCe0.85-xZr xY0.15O3-´ solid electrolytes using impedance spectroscopy" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• CESARE PAGURA (Persona)
• MONICA FABRIZIO (Unità di personale interno)
• LIOUDMILA DOUBOVA (Unità di personale interno)
• CECILIA MORTALO' (Unità di personale interno)
• SIMONA BARISON (Persona)
• STEFANO BOLDRINI (Persona)

Prodotto

• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)
• Leghe metalliche e ossidi nanostrutturati per dispositivi IT-SOFC, per nanofluidi, per materiali termoelettrici e loro applicazioni industriali (ET.P06.009.001) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of Applied Electrochemistry (Rivista)

Insieme di parole chiave di

• Parole chiave di "Conductivity studies of sol-gel prepared BaCe0.85-xZr xY0.15O3-´ solid electrolytes using impedance spectroscopy" (Insieme di parole chiave)