Thermal diffusivity of Ni–Ti SMAs (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Thermal diffusivity of Ni–Ti SMAs (Articolo in rivista) (literal)

Anno

• 2009-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.jallcom.2008.05.040 (literal)

Alternative label

• C. Zanotti; P. Giuliani; G. Riva; A. Tuissi; A. Chrysanthou (2009)
  Thermal diffusivity of Ni–Ti SMAs
  in Journal of alloys and compounds
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• C. Zanotti; P. Giuliani; G. Riva; A. Tuissi; A. Chrysanthou (literal)

Pagina inizio

• 231 (literal)

Pagina fine

• 237 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 473 (literal)

Rivista

• Journal of alloys and compounds (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 1-2 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Institute for Energetics and Interphases, Via R. Cozzi 53, Milano, Italy b Institute for Energetics and Interphases, Corso Promessi Sposi 29, Lecco, Italy c University of Hertfordshire, College Lane, Hatfield, UK (literal)

Titolo

• Thermal diffusivity of Ni–Ti SMAs (literal)

Abstract

• In this paper thermal diffusivity dependence on temperature of NiTi SMAs alloy in the range from 300 K up to 1500 K is reported and the experimental-numerical approach adopted for this scope is described. The experimental work is based on the capability to heat the NiTi sample by means of laser radiation and to record the temperature history at different positions of the sample and afterwards on the possibility to reproduce the experimental curves by numerical computations. A variety of heating rates ranging from 2 K/s to 100 K/s and maximum temperature values (600-1500 K) at the top of the NiTi sample, were used to carry out experiments featured by different heating transients. The numerical code, based on the 1 D unsteady heat diffusion equation, was observed to be in very good agreement with the experimental results and the thermal diffusivity value that was obtained showed drastic changes during the phase transition that occurred during the martensitic transformation. (C) 2008 Elsevier B.V. All rights reserved. (literal)

Prodotto di

• Modelli teorico-computazionali per i materiali (ET.P06.005.002) (Modulo)
• X TRANSIZIONE PD-LC Tecnologia e sviluppo di materiali metallici semilavorati, leghe a memoria di forma e di componenti funzionali per applicazioni di energetica e nel settore trasporti (ET.P06.007.001) (Modulo)
• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)

Autore CNR

• GIULIO RIVA (Unità di personale interno)
• PIETRO GIULIANI (Persona)
• AUSONIO TUISSI (Persona)
• CLAUDIO ZANOTTI (Unità di personale interno)

Incoming links:

Autore CNR di

• PIETRO GIULIANI (Persona)
• GIULIO RIVA (Unità di personale interno)
• AUSONIO TUISSI (Persona)
• CLAUDIO ZANOTTI (Unità di personale interno)

Prodotto

• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)
• X TRANSIZIONE PD-LC Tecnologia e sviluppo di materiali metallici semilavorati, leghe a memoria di forma e di componenti funzionali per applicazioni di energetica e nel settore trasporti (ET.P06.007.001) (Modulo)
• Modelli teorico-computazionali per i materiali (ET.P06.005.002) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of alloys and compounds (Rivista)